PRODUCT DATA SHEET
Sikaflex®-11 FC
ONE PART ADVANCED POLYURETHANE, ELASTOMERIC SEALANT/ADHESIVE
DESCRIPTION CHARACTERISTICS / ADVANTAGES
Sikaflex®-11 FC is a one-component, gun-grade, adhes- ▪ Excellent adhesion on all cement-based materials,
ive and sealing compound of permanent elasticity. This brick, ceramics, glass, metals, wood, epoxy, polyes-
dual-purpose material is based on a special moisture- ter and acrylic resin.
cured polyurethane with an accelerated curing time ▪ Fast cure rate.
that meets ASTM C920 Type S, Grade NS, Class 12.5, ▪ Good weathering and water resistance.
Use NT, I, M, G, A, O. and Federal Specification TT-S- ▪ Non-corrosive.
00230C. ▪ Can be painted over with water, oil, and rubber-
based paints. (Preliminary tests recommended).
USES ▪ High durability.
As an elastic adhesive for:
▪ Cover plates, gaskets and coverings.
▪ Acoustic ceiling tiles.
▪ Floor moldings and door sills.
▪ Light weight construction materials.
▪ Wood or metal and door frames.
▪ Roof tiles.
As an elastic joint sealer for:
▪ Air ducts and high vacuum systems.
▪ Containers, tanks, and silos.
▪ Gaskets in openings in walls or floors for ducts, piling,
etc.
▪ Reservoirs or water retaining structures.
▪ Aluminum fabrication.
▪ Bolted lap joints.
PRODUCT INFORMATION
Packaging Disposable 10.1 fl. oz., moisture-proof composite cartridges, 24/case.
Colour White
Shelf Life 12 months in unopened container.
Storage Conditions Store at 40–95 °F (4–35 °C).
Condition material to 65–75 °F before using.
Volatile organic compound (VOC) con- 28.5 g/L
tent
Product Data Sheet
Sikaflex®-11 FC
December 2018, Version 01.01
020513010000000008
1/3
TECHNICAL INFORMATION
Shore A Hardness 40–45 (73 °F (23 °C) and 50 % R.H.) (ASTM D-2240)
Tensile Strength 225 psi (73 °F (23 °C) and 50 % R.H.) (ASTM D-412)
Elongation at Break 600 % (73 °F (23 °C) and 50 % R.H.) (ASTM D-412)
Elastic Recovery >90 % (73 °F (23 °C) and 50 % R.H.) (ASTM C-719)
Lap Shear Strength 165 psi (73 °F (23 °C) and 50 % R.H.) (ASTM D-1002
modified, glass substrate)
Chemical Resistance Good resistance to water, weak acids, weak alkalis, sewerage, mineral oils,
vegetable oils, fats, fuels. (Not resistant to organic solvents, paint thinner,
strong acids, strong alkalis). Consult Technical Service for specific data.
Service Temperature -40 °F to 170 °F
Resistance to Weathering Excellent
APPLICATION INFORMATION
Consumption Width/Depth 1/4'' 3/8'' 1/2''
1/4'' 24.3
3/8'' 16.2 10.8
1/2'' 12.1 8.1 6.1
3/4'' 8.1 5.4 4.0
1'' 3.0
1.25'' 2.4
1.5'' 2.0
Product Temperature
Ambient Air Temperature 40 °F to 100 °F.
Sealant should be installed when joint is at mid-range of its anticipated
movement.
Curing Rate Tack-free Time (TT-S-00230C) 1 to 2 hours depending on climate
Final Cure 3 to 5 days
APPLICATION INSTRUCTIONS the sealant; continue on with a steady flow of sealant
preceding the nozzle to avoid air entrapment. Avoid
SUBSTRATE PREPARATION overlapping of sealant to eliminate entrapment of air.
Clean all surfaces. Joint walls must be sound, clean, Tooling and Finishing
dry, frost-free, and free of oil and grease. Curing com- Tool as required. Joint dimension should allow for 1/4
pound residues and any other foreign matter mustbe inch minimum and 1/2 inch maximum thickness for
thoroughly removed. A roughened surface will also en- sealant. Proper design is 2:1 width to depth ratio.
hance bond.
Removal
Priming In case of spills of leaks, wear suitable protective
Priming is not usually necessary for anodized alumin- equipment, contain spill, collect with absorbent mater-
um, steel, non-absorbent materials such as glass, ial, and transfer to suitable container. Ventilate area.
ceramics, stoneware and tiles. Most substrates only Avoid contact. Dispose of in accordance with current,
require priming if testing indicates a need or where applicable local, state, and federal regulations. In case
sealant will be subjected to water immersion after of emergency, call chemtrec 1-800-424-9300.
cure. Consult Technical Service at 1-800-933-SIKA for
additional information on priming. Over Painting
Allow 5 day cure at standard conditions when using
APPLICATION METHOD / TOOLS Sikaflex-11 FC in total water immersion situations and
prior to painting.
Recommended application temperatures: 40–100 °F.
For cold weather application, condition material to
65–75 °F before using. Place nozzle of gun into bot-
tom of the joint and fill entire joint. Keep the nozzle in
Product Data Sheet
Sikaflex®-11 FC
December 2018, Version 01.01
020513010000000008
2/3
LIMITATIONS ECOLOGY, HEALTH AND SAFETY
▪ Allow 5 day cure at standard conditions when using For information and advice on the safe handling, stor-
Sikaflex®-11 FC in total water immersion situations age and disposal of chemical products, users shall refer
and prior to painting. to the most recent Safety Data Sheet (SDS) containing
▪ Avoid exposure to high levels of chlorine. (Maximum physical, ecological, toxicological and other safety-re-
level is 5ppm). lated data.
▪ Maximum depth of sealant must not exceed 1/2 in.;
minimum depth is 1/4 in. LEGAL NOTES
▪ Maximum expansion and contraction should not ex-
ceed 12.5 % of average joint width. The information, and, in particular, the recommenda-
▪ Avoid contact with alcohol and other solvent clean- tions relating to the application and end-use of Sika
ers during cure. products, are given in good faith based on Sika's cur-
▪ Do not apply when moisture-vapor-transmission con- rent knowledge and experience of the products when
dition exists from the substrate as this can cause properly stored, handled and applied under normal
bubbling within the sealant. conditions in accordance with Sika's recommenda-
▪ Use opened cartridges the same day. tions. In practice, the differences in materials, sub-
▪ When applying sealant, avoid air-entrapment. strates and actual site conditions are such that no war-
▪ Since system is moisture-cured, permit sufficient ex- ranty in respect of merchantability or of fitness for a
posure to air. particular purpose, nor any liability arising out of any
▪ White color tends to yellow slightly when exposed to legal relationship whatsoever, can be inferred either
ultraviolet rays. from this information, or from any written recom-
▪ The ultimate performance of Sikaflex®-11 FC de- mendations, or from any other advice offered. The
pends on proper application, good design and prop- user of the product must test the product’s suitability
er preparation of joint surfaces. for the intended application and purpose. Sika re-
▪ Not for use in expansion joints. serves the right to change the properties of its
▪ Heavier substrates may require additional support products. The proprietary rights of third parties must
during the cure period. be observed. All orders are accepted subject to our
▪ Do not use in contact with bituminous/asphaltic ma- current terms of sale and delivery. Users must always
terials. refer to the most recent issue of the local Product Data
Sheet for the product concerned, copies of which will
BASIS OF PRODUCT DATA be supplied on request.
All technical data stated in this Product Data Sheet are
based on laboratory tests. Actual measured data may
vary due to circumstances beyond our control.
LOCAL RESTRICTIONS
Please note that as a result of specific local regula-
tions the declared data for this product may vary from
country to country. Please consult the local Product
Data Sheet for the exact product data.
Sika India Pvt. Ltd.
620, Diamond Harbour Road
Commercial Complex II
Kolkata - 700 034
Tel : +91 33 24472448
Fax : +91 33 23978688
Mail :
[email protected] Sikaflex-11FC-en-IN-(12-2018)-1-1.pdf
Product Data Sheet
Sikaflex®-11 FC
December 2018, Version 01.01
020513010000000008
3/3