LUPOY GP1000MU

Injection Molding, PC, Non-flame Retardancy

Description Application
General Purpose , UV Resistant Auto, Electronics, Home Appliances, Industrial Goods

Properties Condition Method Unit Typical Value

Physical
Specific Gravity 23℃ ISO 1183 1.20
Shrinkage 1 ISO 294-4 1 ,
Flow 2.0mm 1 % 0.6~0.8
Cross-flow 2.0mm 1 % 0.7~0.9
Melt Flow Rate 300℃, 1.2kg ISO 1133 g/10min 11
Water Absorption 23°C, 50% RH ISO 62 % 0.20

Mechanical
Tensile Strength 1 ISO 527 1 ,
@Yield 4.0mm, 50mm/min 1 MPa 62
@Break 4.0mm, 50mm/min 1 MPa 70
Tensile Elongation 1 ISO 527 1 ,
@Yield 4.0mm, 50mm/min 1 % 6.0
@Break 4.0mm, 50mm/min 1 % 138
Tensile Modulus 4.0mm, 1mm/min ISO 527 MPa 2,330
Flexural Strength 4.0mm, 2.0mm/min ISO 178 MPa 100
Flexural Modulus 4.0mm, 2.0mm/min ISO 178 MPa 2,310
IZOD Impact Strength 1 ISO 180 1 ,
4.0mm, Notched 23℃ 1 kJ/m² 71
1 -30℃ 1 kJ/m² 9.0
1 -40℃ 1 kJ/m² 9.0
Charpy Impact Strength 1 ISO 179 1 ,
4.0mm, Notched 23℃ 1 kJ/m² 73
1 -30℃ 1 kJ/m² 10
1 -40℃ 1 kJ/m² 10
Rockwell Hardness R-Scale ISO 2039 118

Thermal
1
Heat Deflection Temperature 4.0mm, Flatwise ISO 75 1 ,
0.45MPa Unannealed 1 ℃ 136
1.8MPa 4.0mm, Flatwise 1 ℃ 121
Unannealed

Note) Typical values can be used only for the purpose of selecting material, and there can be variation within normal tolerances for various colors.
Values given should not be interpreted as specification and not be used for designing part or tool.
All properties, except melt flow rate are measured by injection molded specimens after 48 hours storage at 23℃, 50% relative humidity.
Issued Date : 2024-07-18

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that
the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice.
Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding
minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each
user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use
conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.
LUPOY GP1000MU
Injection Molding, PC, Non-flame Retardancy

Description Application
General Purpose , UV Resistant Auto, Electronics, Home Appliances, Industrial Goods

Vicat Softening Temperature 50N, 50℃/hr ISO 306 ℃ 142

Coefficient of Linear Thermal Expansion 1 ISO 11359 1 ,
Flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 77
Cross-flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 79

Flammability
Flammability UL94 1 ,
1
1 1 mm, Class 0.37mm, HB
Relative Temperature Index(RTI) 1 UL746B 1 ,
Electrical Min. Thickness 1 mm 0.37
1 Temp 1 ℃ 80
1 Max. Temp 1 ℃ 130
1 Thickness 1 mm 1.50
Mechanical With Impact Min. Thickness 1 mm 0.37
1 Temp 1 ℃ 80
1 Max. Temp 1 ℃ 130
1 Thickness 1 mm 1.50
Mechanical Without Impact Min. Thickness 1 mm 0.37
1 Temp 1 ℃ 80
1 Max. Temp 1 ℃ 130
1 Thickness 1 mm 1.50

Electrical
Comparative Tracking Index(CTI) Solution A UL746A PLC 2
Surface Resistivity 23℃ IEC60093 Ohm 1E+15
Volume Resistivity 23℃ IEC60093 Ohm·m 1E+15
Dielectric Constant 23°C ASTM D150 2.8
Dielectric Strength 23℃, 2.0mm ASTM D149 kV/mm 21

Note) Typical values can be used only for the purpose of selecting material, and there can be variation within normal tolerances for various colors.
Values given should not be interpreted as specification and not be used for designing part or tool.
All properties, except melt flow rate are measured by injection molded specimens after 48 hours storage at 23℃, 50% relative humidity.
Issued Date : 2024-07-18

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that
the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice.
Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding
minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each
user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use
conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.
LUPOY GP1000MU
Injection Molding, PC, Non-flame Retardancy

Description Application
General Purpose , UV Resistant Auto, Electronics, Home Appliances, Industrial Goods

Processing Conditions (Injection Molding)

Processing Parameters Unit Value

Drying Temperature ℃ 100~120

Drying Time hrs 3~5

Maximum Moisture Content % 0.02

Melt Temperature ℃ 300~320

Rear ℃ 260~280

Cylinder Temperature Middle ℃ 280~300

Front ℃ 300~320

Nozzle Temperature ℃ 300~320

Mold Temperature ℃ 80~120

Note) These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.

Note) Typical values can be used only for the purpose of selecting material, and there can be variation within normal tolerances for various colors.
Values given should not be interpreted as specification and not be used for designing part or tool.
All properties, except melt flow rate are measured by injection molded specimens after 48 hours storage at 23℃, 50% relative humidity.
Issued Date : 2024-07-18

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that
the result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice.
Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding
minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each
user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use
conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.