WHD630/315 Welding Parameters for PE pipes and fittings.
According to DVS 2207 T1
(dual pressure and low fusion jointing pressure procedure)
PE 80: Temperature of heating element between 200°C - 220°C
for lower wall thickness use upper temperature level.
PE100: Temperature of heating element between 210°C - 230°C
T2 and T3 should be as short as possible
welding pressure 0.15 Mpa soaking pressure 0.01 Mpa
Hydraulic cylinder max. Hydr.
area 2306 mm² Pressure 16 Mpa
T1 min. bead height at heating element
Bead width
Pipe after
Dimension SDR P1 T1 P2 T2 T3 T4 P3 T5 cooling
(add (add
max. max.
OD Wall drag) drag) Min Max
mm mm Mpa mm Mpa sec sec sec Mpa Min mm mm
315 7.7 41 0.48 1.5 0.0 115 8 8 0.48 10 7 11
315 9.7 33 0.61 1.5 0.0 146 8 8 0.61 10 8 12
315 12.1 26 0.75 2.0 0.0 182 10 11 0.75 16 9 14
315 15.0 21 0.92 2.0 0.1 225 10 11 0.92 16 11 16
315 18.7 17 1.13 2.0 0.1 281 10 11 1.13 16 12 19
315 23.2 13.6 1.38 2.5 0.1 347 12 14 1.38 24 15 22
315 28.6 11 1.68 3.0 0.1 430 16 19 1.68 32 17 26
315 35.2 9 2.01 3.0 0.1 528 16 19 2.01 32 21 31
315 43.1 7.4 2.39 3.5 0.2 647 20 25 2.39 45 25 37
355 8.7 41 0.61 1.5 0.0 130 8 8 0.61 10 7 11
355 10.9 33 0.77 1.5 0.1 164 8 8 0.77 10 8 13
355 13.6 26 0.95 2.0 0.1 204 10 11 0.95 16 10 15
355 16.9 21 1.17 2.0 0.1 254 10 11 1.17 16 11 18
355 21.1 17 1.44 2.5 0.1 317 12 14 1.44 24 14 21
355 26.1 13.6 1.75 3.0 0.1 392 12 14 1.75 24 16 25
355 32.2 11 2.12 3.0 0.1 483 16 19 2.12 32 19 29
355 39.4 9 2.54 3.5 0.2 592 20 25 2.54 45 23 35
355 48.0 7.4 3.01 3.5 0.2 720 20 25 3.01 45 27 41
400 9.8 41 0.78 1.5 0.1 146 8 8 0.78 10 8 12
400 12.3 33 0.97 2.0 0.1 185 10 11 0.97 1 9 14
400 15.3 26 1.20 2.0 0.1 230 10 11 1.20 16 11 16
400 19.1 21 1.49 2.0 0.1 287 10 11 1.49 16 13 19
400 23.7 17 1.82 2.5 0.1 356 12 14 1.82 24 15 23
400 29.4 13.6 2.23 3.0 0.1 441 16 19 2.23 32 18 27
400 36.3 11 2.70 3.0 0.2 545 16 19 2.70 32 21 32
400 44.4 9 3.23 3.5 0.2 667 20 25 3.23 45 25 38
400 54.1 7.4 3.82 4.0 0.3 811 25 35 3.82 50 30 46
WORLDPOLY AUSTRALIA www.worldpoly.com [email protected]
14
Bead width
Pipe after
Dimension SDR P1 T1 P2 T2 T3 T4 P3 T5 cooling
(add (add
max. max.
OD Wall drag) drag) Min Max
mm mm Mpa mm Mpa sec sec sec Mpa Min mm mm
450 11.0 41 0.98 1.5 0.1 165 8 8 0.98 10 8 13
450 13.8 33 1.23 2.0 0.1 207 10 11 1.23 16 10 15
450 17.2 26 1.52 2.0 0.1 258 10 11 1.52 16 12 18
450 21.4 21 1.87 2.5 0.1 321 12 14 1.87 24 14 21
450 26.7 17 2.31 3.0 0.2 401 16 19 2.31 32 16 25
450 33.1 13.6 2.82 3.0 0.2 496 16 19 2.82 32 20 30
450 40.9 11 3.42 3.5 0.2 614 20 25 3.42 45 23 36
450 50.3 9 4.11 4.0 0.3 755 20 25 4.11 45 28 43
450 61.5 7.4 4.88 4.0 0.3 923 25 35 4.88 50 34 51
500 12.3 41 1.23 2.0 0.1 185 10 11 1.23 16 9 14
500 15.3 33 1.52 2.0 0.1 230 10 11 1.52 16 11 16
500 19.1 26 1.88 2.0 0.1 287 12 14 1.88 24 13 19
500 23.9 21 2.33 2.5 0.2 359 12 14 2.33 24 15 23
500 29.6 17 2.85 3.0 0.2 444 16 19 2.85 32 18 27
500 36.8 13.6 3.48 3.0 0.2 551 16 19 3.48 32 21 33
500 45.4 11 4.22 3.5 0.3 681 20 25 4.22 45 26 39
500 56 9 5.08 4.0 0.3 840 25 35 5.08 50 31 47
500 68.3 7.4 6.03 4.0 0.4 1025 25 35 6.03 50 37 56
560 13.7 41 1.52 2.0 0.1 205 10 11 1.52 16 10 15
560 17.2 33 1.91 2.0 0.1 258 10 11 1.91 16 12 18
560 21.4 26 2.36 2.5 0.2 321 12 14 2.36 24 14 21
560 26.7 21 2.91 3.0 0.2 400 16 19 2.91 32 16 25
560 33.2 17 3.57 3.0 0.2 498 16 19 3.57 32 20 30
560 41.2 13.6 4.37 3.5 0.3 618 20 25 4.37 45 24 36
560 50.8 11 5.29 3.5 0.4 762 20 25 5.29 45 28 43
560 62.2 9 6.33 4.0 0.4 933 25 35 6.33 50 34 52
560 75.7 7.4 7.49 4.0 0.5 1135 25 35 7.49 50 41 62
630 15.4 41 1.93 2.0 0.1 230 10 11 1.93 16 11 17
630 19.3 33 2.41 2.5 0.2 290 12 14 2.41 24 13 19
630 24.1 26 2.98 2.5 0.2 362 12 14 2.98 24 15 23
630 30.0 21 3.68 3.0 0.2 450 16 19 3.68 32 18 28
630 37.3 17 4.52 3.0 0.3 560 16 19 4.52 32 22 33
630 46.3 13.6 5.53 3.5 0.4 695 20 25 5.53 45 26 40
630 57.2 11 6.70 4.0 0.4 858 25 25 6.70 45 32 48
630 70.0 9 8.01 4.0 0.5 1050 25 35 8.01 50 38 58
630 85.1 7.4 9.48 5.0 0.6 1277 25 35 9.48 50 46 69