Quality 42crmo4 Chemical Composition: Technical Card Gruppo Lucefin Revision 2012 All Rights Reserved

This document provides information on the chemical composition, heat treatment processes, mechanical properties, and other technical specifications of the steel grade 42CrMo4. Some key points include: - The chemical composition ranges for 42CrMo4 steel according to EN 10269 standards. - Recommended heat treatment processes and temperatures for processes like normalizing, quenching, tempering, and stress relieving. - Minimum property requirements for mechanical properties like tensile strength, yield strength, elongation and impact toughness at different temperatures. - Data on properties like thermal expansion, modulus of elasticity, specific heat, and fatigue strength. - Equivalent grades of 42CrMo4 steel according to different international

Uploaded by

Vijayakumar Samy
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
81 views2 pages

Quality 42crmo4 Chemical Composition: Technical Card Gruppo Lucefin Revision 2012 All Rights Reserved

This document provides information on the chemical composition, heat treatment processes, mechanical properties, and other technical specifications of the steel grade 42CrMo4. Some key points include: - The chemical composition ranges for 42CrMo4 steel according to EN 10269 standards. - Recommended heat treatment processes and temperatures for processes like normalizing, quenching, tempering, and stress relieving. - Minimum property requirements for mechanical properties like tensile strength, yield strength, elongation and impact toughness at different temperatures. - Data on properties like thermal expansion, modulus of elasticity, specific heat, and fatigue strength. - Equivalent grades of 42CrMo4 steel according to different international

Uploaded by

Vijayakumar Samy
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Quality 42CrMo4

Tecnn|ca| caro
According to standards EN 10269 (AC: 2008)
Lucefin Croup
Number 1.7225 rev. 20'2

Chemical composition
C% Si%
max
Mn% P%
max
S%
max
Cr%

Mo%



Product deviations are
allowed
0,380,45 0,40 0,600,90 0,025 0,035 0,901,20 0,150,30
0.02 + 0.03 0.04 + 0.005 + 0.005 0.05 0.03

Temperature C
Hotforming Normalizing
+N
Quenching
+Q
Quenching
+Q
Tempering
+T
Stressrelieving
+SR
1100850 870
air
860
oil or polymer
850
water
540680
air
50 under the
temperature of tempering
Soft
annealing +A
Isothermal
annealing +I
Spheroidizing
annealing +AC
End quench
hardenability test
Preheating welding Stressrelieving
after welding
720
air
(HB max 241)
820 furnace cooling
to 670, then air
(HB 180240)
730740
furnace cooling
(HB max 200)
840
water
300 550 furnace cooling
AC1 AC3 MS Mf
745 790 335 120

Mechanical properties
Hotrolled +QT EN 10269 (AC: 2008)
size mm Kv and traction test at room temperature in longitudinal
R Rp 0.2 A% C% Kv +20 C Kv 40 C Kv 100 C h8
from to N/mm
2
. N/mm
2
min. min. min. J min. J min. J min.
60 8601060 730 14 50 50 40 27 258-J22
+QT = quenched and tempered

Min. proof strength 0.2 % at high temperatures Rp 0.2 N/mm
2
EN 10269: 2001
d. max 60 mm 720 702 677 640 602 562 518 475 420 375
C 50 100 150 200 250 300 350 400 450 500 550

Plastic deformations and creep rupture resistance
1(1%) N/mm
2
R N/mm
2

C 10.000 h 100.000 h 10.000 h 100.000 h
450 190 137 320 240
500 88 49 137 96
550 29 15 29 15
1 = permanent creep strain strength 1% R = creep rupture strength

Thermal Expansion
10
6
K
1


12.1 12.7 13.2 13.6 14.0 14. 4
Mod. of Elasticity long. GPa 210 205 195 185 175 155
Mod. of Elasticity tang. GPa 80 78 75 70 67 59
Specific Heat Capacity J/(KgK) 460
Thermal Conductivity W/(mK) 33.5 34.0 34.2
Density Kg/dm
3
7.85
Specific Electric Resist. Ohmmm
2
/m 0.19
Electrical Conductivity Siemensm/mm
2
5.26
C 20 100 200 250 300 400 500 600
The symbol indicates temperature between 20 C and 100 C, 20 C and 200 C

Kv and traction test at room temperature in longitudinal on hotrolled +QT material. Lucefin experience
diameter
mm
grain
size
R Rp 0.2 Rp/R A% C% Kv +20 C Kv 20 C
N/mm
2
N/mm
2
min. min. J min. J min.
40 6 995 845 0,85 15,2 58 909092 605858
60 56 947 767 0,81 16.0 60 847880 505056









TECHNICAL CARD
GRUPPO LUCEFIN
REVISION 2012
ALL RIGHTS RESERVED

42CrMo4 1.7225

Data under fatigue +20 C
+N 328 Cyclic yield strength, y
N/mm
2
low cycle number



+QT 716
+N 0.12 Cyclic strength exponent, n
low cycle number

+QT 0.10
+N 673 Cyclic strength coefficient, K
N/mm
2
low cycle number

+QT 1367
+N 1000 Fatigue strength coefficient, f
N/mm
2
low cycle number



+QT 1454
+N 0.11 Fatigue strength exponent, b
low cycle number



+QT 0.08
+N 1.00 Fatigue ductility exponent, c
low cycle number



+QT 0.72
+N = normalization +QT = quenching and tempering



EUROPE
EN
ITALY
UNI
CHINA
GB
GERMANY
DIN
FRANCE
AFNOR
U.K.
B.S.
RUSSIA
GOST
USA
AISI/SAE
42CrMo4 42CrMo4 ML42CrMo 42CrMo4 42CD4 708M40 42HM 4140


THE DATA CONTAINED HEREIN ARE INTENDED AS REFERENCE ONLY AND ARE SUBJECT TO CONSTANT CHANGE. LUCEFIN S.P.A. DISCLAIMS ANY AND ALL LIABILITY FOR ANY CONSEQUENCES THAT MAY RESULT FROM THEIR USE.