201861 ASM Material Data Sheet
Titanium Ti6Al4V (Grade 5), Annealed
Subcategory: Alpha/Beta Titanium Alloy; Metal; Nonferrous Metal; Titanium Alloy
Close Analogs: 4 other heat treatments of this alloy are listed in MatWeb.
Key Words: Ti64; UNS R56400; ASTM Grade 5 titanium; UNS R56401 (ELI); Ti6Al4V, biomaterials,
biomedical implants, biocompatibility
Component Wt. %
Al 6
Fe Max 0.25
O Max 0.2
Ti 90
V 4
Material Notes:
Information provided by Allvac and the references. Annealing Temperature 700785ºC. AlphaBeta Alloy.
Applications: Blades, discs, rings, airframes, fasteners, components. Vessels, cases, hubs, forgings. Biomedical implants.
Biocompatibility: Excellent, especially when direct contact with tissue or bone is required. Ti6Al4V's poor shear strength
makes it undesirable for bone screws or plates. It also has poor surface wear properties and tends to seize when in sliding
contact with itself and other metals. Surface treatments such as nitriding and oxidizing can improve the surface wear properties.
Physical Properties Metric English Comments
Density 4.43 g/cc 0.16 lb/in³
Mechanical Properties
Hardness, Brinell 334 334 Estimated from Rockwell C.
Hardness, Knoop 363 363 Estimated from Rockwell C.
Hardness, Rockwell C 36 36
Hardness, Vickers 349 349 Estimated from Rockwell C.
Tensile Strength, Ultimate 950 MPa 138000 psi
Tensile Strength, Yield 880 MPa 128000 psi
Elongation at Break 14 % 14 %
Reduction of Area 36 % 36 %
Modulus of Elasticity 113.8 GPa 16500 ksi
Compressive Yield Strength 970 MPa 141000 psi
Notched Tensile Strength 1450 MPa 210000 psi Kt (stress concentration factor) = 6.7
Ultimate Bearing Strength 1860 MPa 270000 psi e/D = 2
Bearing Yield Strength 1480 MPa 215000 psi e/D = 2
Poisson's Ratio 0.342 0.342
http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=mtp641 1/2
201861 ASM Material Data Sheet
Charpy Impact 17 J 12.5 ftlb Vnotch
Fatigue Strength 240 MPa 34800 psi at 1E+7 cycles. Kt (stress concentration factor) = 3.3
Fatigue Strength 510 MPa 74000 psi Unnotched 10,000,000 Cycles
Fracture Toughness 75 MPam½ 68.3 ksiin½
Shear Modulus 44 GPa 6380 ksi
Shear Strength 550 MPa 79800 psi Ultimate shear strength
Electrical Properties
Electrical Resistivity 0.000178 ohmcm 0.000178 ohmcm
Magnetic Permeability 1.00005 1.00005 at 1.6kA/m
Magnetic Susceptibility 3.3e006 3.3e006 cgs/g
Thermal Properties
CTE, linear 20°C 8.6 µm/m°C 4.78 µin/in°F 20100ºC
CTE, linear 250°C 9.2 µm/m°C 5.11 µin/in°F Average over the range 20315ºC
CTE, linear 500°C 9.7 µm/m°C 5.39 µin/in°F Average over the range 20650ºC
Specific Heat Capacity 0.5263 J/g°C 0.126 BTU/lb°F
Thermal Conductivity 6.7 W/mK 46.5 BTUin/hrft²°F
Melting Point 1604 1660 °C 2920 3020 °F
Solidus 1604 °C 2920 °F
Liquidus 1660 °C 3020 °F
Beta Transus 980 °C 1800 °F
References for this datasheet.
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistant format.
Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to
equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you
refer to MatWeb's disclaimer and terms of use regarding this information. MatWeb data and tools provided by MatWeb, LLC.
http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=mtp641 2/2