Technical Data Sheet
[email protected]
Performance Additives
Decorative
LAVIOTHIX® P100
Rheological additive for water borne system
General information Applications
®
LAVIOTHIX P100 is product of inorganic origin • Adhesives
based on clay, with high performances and • Emulsion paints
efficiency, specific for water borne formulations • Bituminous emulsion
that gives great pseudoplastic behaviour and • Latex paints
tixotropy.
Il LAVIOTHIX
®
P100 is a thickening and Properties
®
antisettling agent, based on a selected, purified LAVIOTHIX P100 is a rheological and
and activated white bentonite clay with a high thixotropical additive that gives stability and
montmorillonite content viscosity control, adhesion control and enhances
Activity is strictly correlated to its hydration texturing and stippling effects.
capacity and to give rise to micronic an It can be incorporated as powder or as an
submicronic particles in dispersion, with a high aqueous 3-4 wt% pregel (Fig. 1)
specific surface; the platelets. These one
®
contribute to create the “body” of the product to be LAVIOTHIX P100 is stable in a wide pH range 2-
formulated by the formation of an internal 12 (Fig 2)
tridimensional structure within which different 20000
particles and fillers may be incorporated 18000
16000
This elementary particles are responsible of the 14000
tixotropic, antisettling, absorbing and binding 12000
Lavio thix P100 2%
cps
10000 Lavio thix P100 3%
properties of the product 8000
Lavio thix P100 4%
6000
Chemical- physical properties 4000
2000
Composition: purified smectite (98% 0
0 20 40 60 80 100 120
montmorillonite) rpm
Physical form: white fine powder Fig.1 : Laviothix P100 pre-gel in water at different concentration
Bulk Density: 0.7-0.8 g/ml
Dry residue: max 3% > 325 mesh (45 µm)
Moisture: max 10%
MO.04.A.G_Eng Rev.01
Laviosa Chimica Mineraria SpA - Italy
Laviosa Sanayi ve Ticaret Ltd Sti - Turkey
Laviosa MPC sas - France
Laviosa Trimex Industries Pvt Ltd - India
20000
18000
10000
16000
9000
14000
8000
7000 12000
high shear
cps
6000 10000
low shear
cps
5000
8000
4000
6000
3000
2000 4000
1000 2000
0 0
0 2 4 6 8 10 12 14 0 20 40 60 80 100 120
pH rpm
Fig.2 : Laviothix P100 pre-gel at 4% in water at different pH values Fig.3 : Laviothix P100 pre-gel in water at 4% using two different shear
rate
Incorporation
® Recommendation
LAVIOTHIX P100 will hydrate when added to
water. To obtain maximum hydration and optimum The viscosity of the slurry could rise during time
performance in the shortest time, we suggest after the preparation, it’s better to measure
following incorporation procedures: viscosity the day after.
®
1. Slowly add LAVIOTHIX and increase shear Dosage
rate to maximum amount which may be
tolerated in the mixing container. Incorporates Typical addition levels are 0.3% - 3.0% of
®
more quickly in warm water. However, do not LAVIOTHIX P100 by weight of total formulation
allow water temperature to rise above 50° C The addition levels depend on the degree of
prior to full hydration. Once hydration has suspension, the rheological properties or viscosity
occurred, there is no temperature limitation for required.
®
LAVIOTHIX Storage stability and packing
2. Continue to disperse until a constant viscosity
is reached (15-30 min) Product do not deteriorate in a significant way in a
3. Add other formula ingredients in appropriate 12 months period. Storage is advisable in a dry,
order sheltered place in closed bags. Packing is 25 kg
net in paper bags.
LAVIOTHIX® P100 shows the same gel formation
properties using either a high shear or a low shear
(Fig 3)
Rev 1 July 2012
Information given in this bulletin is based on the state of our knowledge at the date of publication and are believed to
be accurate, but do not constitute any engagement or warranty from our part. Buyers and users should make their
own assessments under their own conditions and for their own requirements. Information may be changed without
any notice. For mandatory characteristics and performance please refer to our Sale Specifications.
MO.04.A.G_Eng