Stainless Steels - "300" Series Stainless Steels - "300" Series

Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa) Typical Values
304 CF-8 A-743-744 J92600 .08 1.50 2.00 .04 .04 18.0-21.0 8.0-11.0 - - 2050°F WQ 70(485) 30(205) 35% 50°F 1900°F WQ 163 .280 Resists strong oxidants
A-351 similar to nitric acid, Autoclaves, filter press plates,
fatty acids, fruit juices hardware, pump parts, valve parts,
spray nozzles, agitators, pump
304L CF-3 A-743-744 J92500 .03 1.50 2.00 .04 .04 17.0-21.0 8.0-12.0 - - 2050°F WQ 70(485) 30(205) 35% 50°F 1900°F WQ 163 .280 Low carbon version of CF-8, sleeves
A-351 (optional) use where post weld heat
treat is not possible
316 CF-8M A-743-744 J92900 .08 1.50 2.00 .04 .04 18.0-21.0 8.0-11.0 2.0-3.0 - 2050°F WQ 70(485) 30(205) 30% 50°F 1900°F WQ 179 .280 Resists reducing solutions Agitators, evaporator parts,
A-351 and pitting in seawater spray nozzles, steam
and black liquors valves, rolls, valve blades
316L CF-3M A-743-744 J92800 .03 1.50 1.50 .04 .04 17.0-21.0 9.0-13.0 2.0-3.0 - 2050°F WQ 70(485) 30(205) 30% 50°F 1900°F WQ 179 .280 Low carbon version of CF-8M, Centrifuges, fittings,
A-351 (optional) use where post weld heat pump parts
treat is not possible
310 CK-20 A-743 J94202 .20 2.00 2.00 .04 .04 23.0-27.0 19.0-22.0 - - 2050°F WQ 65(450) 28(195) 30% 50°F 2000°F WQ 163 .280 Withstands elevated Digester, filter press parts,
A-351 temperatures, resists dilute fittings, pumps, valves
sulfuric acid, sulfite liquors
347 CF-8C A-743-744 J92710 .08 1.50 2.00 .04 .04 18.0-21.0 9.0-12.0 - Cb=8x%C 2050°F WQ 70(485) 30(205) 30% 50°F 1900°F WQ 156 .280 Suitable for field welding, Autoclaves, chemical tubing,
A-351 not more than 1% (optional) stabilized grade of CF-8 fittings, valves, pump parts
317 CG-8M A-743-744 J93000 .08 1.50 1.50 .04 .04 18.0-21.0 9.0-13.0 3.0-4.0 - 2050°F WQ 75(520) 35(240) 25% 50°F 1900°F WQ 176 .280 Improved corrosion Same as CF-8M
A-351 resistance compared to CF-8M
317L CG-3M A-743-744 S31703 .03 1.50 1.50 .04 .04 18.0-21.0 9.0-13.0 3.0-4.0 - 2050F WQ 75(515) 35(240) 25% 50°F 1900°F WQ 179 .280 Low carbon version of CG-8M Same as CF-3M
(optional) for improved weldability
Nitronic60® CF10SMnN A-351 S21800 .10 7.00-9.00 3.50-4.50 .060 .030 16.0-18.0 8.0-9.0 - N.08-.18 2050°F WQ 85(585) 35(240) 30% 50°F 2050°F WQ 179 .285 Austenitic S.S strengthened Valves & pumps exposed
A-743-744 with N, corrosion resistance to acid and chloride. Deep
exceeds 304 & 316 well sour gas
Nitronic50® CG6MMN A-351 S20910 .06 4.00- 1.00 .04 .03 20.5-23.5 11.5-13.5 1.50-3.00 Cb.10-.30 2050°F WQ 85(585) 42(290) 30% 50°F 1950°F WQ 200 .279 Wholly austenitic with wear Oil field sensing equipment.
A-743-744 6.00 and corrosion resistance Low magnetic permeability
superior to 304 & 316 applications
20Cb-3® CN-7M A-743-744 N08020 .07 1.50 1.50 .04 .04 19.0-22.0 27.5-30.5 2.0-3.0 Cu 3.0-4.0 2050°F WQ 62(425) 25(170) 35% 50°F 2050°F WQ 156 .289 Resists sulfuric acid, reducing Pickling rolls, hooks, racks,
A-351 chemicals, hydrochloric acid, pulp and paper, food
not chlorides and nitric acid processing, plastics

Stainless Steels - "400" Series Stainless Steels - "400" Series

Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa) Typical Values
410 CA-15 A-743 J91150 .15 1.00 1.50 .04 .04 11.5-14.0 1.00 max .50 max - 1850°F AQ 90(620) 65(450) 18% 207
A-487 1100°F AQ for
A-217 ASTM A-743
1850°F AQ 200(1378) 150(1034) 7% 390 Hardenability to 189-400 BHN. Pump castings, liners, valve trim,
600°F AQ typical typical typical 400°F 1100-1400°F Good atmospheric corrosion fittings, burner tips,
1850°F AQ 135(930) 115(792) 17% 260 .275 resistance skimmer ladles
1100°F AQ typical typical typical
1850°F AQ 115(792) 100(690) 22% 225
1200°F AQ typical typical typical
416 416 - S41600 .15 1.00 1.50 .04 .20 12.0-14.0 1.00 max .60 max Se.03 max 1850°F AQ 80(551) 40(275) 25% 400°F 1100-1400°F 212 .275 Free machining grade Same as CA-15
1200°F AQ similar to CA-15
420 CA-40 A-743 J91153 .20-.40 1.00 1.50 .04 .04 11.5-14.0 1.0 max .5 max - 1850°F AQ 100(690) 70(485) 15% 240
A-487 1100°F AQ for
ASTM A-743
1850°F AQ 220(1516) 165(1137) 1% 470 Hardenability up to 500BHN. Choppers, cutting
600°F AQ typical typical typical 400°F 1100-1400°F Corrosion resistance same as blades, cylinder liners,
CA-15 pump parts, rolls
1850°F AQ 150(1034) 125(861) 10% 310
1100°F AQ typical typical typical
1850°F AQ 140(965) 125(861) 10% 267
1200°F AQ typical typical typical
420F CA-40F A-743 S42020 .20-.40 1.00 1.50 .04 .20-.40 11.5-14.0 1.0 max .5 max - - Heat Treat and Physical Properties same as CA-40, Elongation is slightly lower over all heat treatments. Free machining grade Same as CA-40
similar to CA-40
431 CB-30 A-743 J91803 .30 1.00 1.50 .04 .04 18.0-21.0 2.00 max - Cu .90-1.20 1450°F AQ 65(450) 30(205) 15% 50°F 1450°F AQ 195 .272 Resists nitric acid. Good Furnace brackets, pump
optional typical machinability, resists sulfur and parts, valve parts
oxidizing atmosphere to 1400°F
- CA-6NM A-743 J91540 .06 1.00 1.00 .04 .03 11.5-14.0 3.5-4.5 .40-1.0 - 1750°F AQ 110(755) 80(550) 15% 50°F 1100- 285 max .278 Hardenability 189 to 400 BHN, Pump casings, liners,
A-487 1050- (RA 35% in) 1400°F AQ good atmospheric and sea valves, skimmer ladles
A-352 1150°F AQ water corrosion resistance,
improved impact strength

Spuncast, Inc. • Tel: 920.261.7853 • E-mail: [email protected] • www.spuncast.com Spuncast, Inc. • Tel: 920.261.7853 • E-mail: [email protected] • www.spuncast.com
 Heat Resistant Alloys Heat Resistant Alloys
Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Maximum Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Usage (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
Temperature KSI(MPa) KSI(MPa)
327 HD A-297 J93005 .50 max 1.50 2.00 .04 .04 26-30 4-7 .5 1950°F 75(515) 35(240) 8% none none 190 .274 High sulfur atmospheres,dual Smelting and steel equipment
phase, non hardenable
312 HE A-297 J93403 .20-.50 2.00 2.00 .04 .04 26-30 8-11 .5 2000°F 85(585) 40(275) 9% none none 200-270 .277 Good oxidation resistance, Sulfur atmospheres,
moderate strength at high temps smelting and steel equipment
302B HF A-297 J92603 .20-.40 2.00 2.00 .04 .04 19-23 9-12 .5 1600°F 70(485) 35(240) 25% none none 165-190 .280 Good oxidation resistance in Tube supports, cement mill parts,
1200-1600°F heat treat furnace parts
309 HH-2 A-447 J93503 .20-.50 2.00 2.00 .04 .04 24-28 11-14 .5 2000°F 75(515) 35(240) 25% none none 185-200 .279 High strength and oxidation Tube supports and beams in oil
(ACI) resistance at high temperatures refineries, heat treat furnaces
- HI A-297 J94003 .20-.50 2.00 2.00 .04 .04 26-30 14-18 .5 2150°F 70(485) 35(240) 10% none none 180-200 .279 Good weldability, resists oxidizing Cast retorts for Mg cyaniding, heat
and reducing atmospheres treating furnace parts
310 HK A-297 J94224 .20-.60 2.00 2.00 .04 .04 24-28 18-22 .5 2100°F 65(450) 35(240) 10% none none 170-190 .280 Resists hot gas corrosion better Tube supports, beams and fittings
than HH, Not recommended for in oil refining, furnace parts
severe thermal shock
310 HK-40 A-351 J94224 .30-.40 2.00 2.00 .04 .04 24-28 18-22 .5 2100°F 65(450) 35(240) 10% none none 170-190 .280 Has higher creep strength than Same as HK
HK due to increased carbon.
- HL A-297 N08604 .20-.60 2.00 2.00 .04 .04 28-32 18-22 .5 2100°F 65(450) 35(240) 10% none none 192 .279 Good corrosion resistance Furnace fixtures, carrier
in sulfur fingers,skids,stacks
- HN A-297 J94213 .20-.50 2.00 2.00 .04 .04 19-23 23-27 .5 2150°F 63(435) - 8% none none 160 .283 Good high temperature strength Brazing fixtures, trays, furnace
and corrosion resistance in parts, radiant tubes
chemical reactive media
- HP A-297 N08705 .35-.75 2.00 2.00 .04 .04 24-28 33-37 .5 2150°F 62.5(430) 34(235) 4.5% none none 190 .284 Excellent strength and oxidation Chemical and oil refinery
resistance at high temperatures tubing and fittings
330 HT A-297 N08605 .35-.75 2.00 2.50 .04 .04 15-19 33-37 .5 2000°F Reducing 65(450) - 4% none none 180-200 .286 High strength and corrosion Heat treating furnace parts,
2100°F Oxidizing resistance at high temps, good rolls, salt pots, glass rolls
for thermal cycling
- HU A-297 N08004 .35-.75 2.00 2.50 .04 .04 17-21 37-41 .5 2000°F Reducing 65(450) - 4% none none 170-190 .290 High strength and corrosion Used for improved hot gas corrosion,
2100°F Oxidizing resistance at high temperatures same as HT, better thermal fatigue
- HW A-297 N08001 .35-.75 2.00 2.50 .04 .04 10-14 58-62 .5 1900°F Reducing 60(415) - - none none 185-205 .294 Excellent service involving Hearths, muffles, retorts, enameling
nonsulfur thermal shock and cyclic heating parts, quenching fixtures
2100°F Oxidizing
- HX A-297 N06006 .35-.75 2.00 2.50 .04 .04 15-19 64-68 .5 1900°F Reducing 60(415) - - none none 176-185 .294 Excellent service involving thermal Same as HW, also contact with
nonsulfur shock and cyclic heating tempering and cyanide salts
2100°F Oxidizing

Nickel Based Alloys, Super Alloys Nickel Based Alloys, Super Alloys
Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa)
50Cr- 50Cr- A-560 - .10 .30 .50 .02 .02 47.0-52.0 bal. - Cb1.4-1.7 max none 80(550) 50(340) 5% 50°F none - .292 Heat resistant, corrosion Structural members, hangers in
50Ni+Cb 50Ni+Cb N.16 max applications, supports and heat treating applications
N+C.20 max hangers up to 2000°F, Cb added
Fe1.00 max for improved weldability
Other alloys with working temperatures of 2100°-2300°F are available upon request Ti.50 max
Al.25 max
Inco625® CW-6MC A-494 N26625 .06 1.00 1.00 .015 .015 20.0-23.0 bal. 8.0-10.0 Fe5.0 max 2150°F AC 70(485) 40(275) 25% none none 163 typical .305 High strength corrosion resistant es- Chemical processing, aerospace,
Cb3.15-4.50 pecially to pitting and crevice corrosion pollution control equipment
Inco600® CY-40 A-494 N06040 .40 1.50 3.00 .03 .03 14.0-17.0 bal. - Fe11.0 max 1900°F AC 70(485) 28(195) 30% 50°F 1900°F WQ - .305 Excellent oxidation resistance Aircraft engine components,
up to 2150°F heat treating equipment
HastB® N12-MV A-494 N30012 .12 1.00 1.00 .040 .030 1.00 bal. 26.0-30.0 Fe4.0-6.0 2050°F WQ 76(524) 40(275) 6% 50°F 2050°F WQ - .334 Corrosion resistant service Centrifuge parts, gas turbine rings
HastC-276® CW-12MW A-494 N30002 .12 1.00 1.00 .040 .030 15.5-17.5 bal. 16.0-18.0 Fe4.5-7.5 2150°F WQ 72(495) 40(275) 4% 50°F 2150°F WQ 192 typical .323 Resistant to chemical solutions, Gas turbine engines, chemical
W3.75-5.25 oxidizing and reducing processing equipment, good
V.20-.40 atmospheres up to 2000°F weldability

Stainless Steels - Duplex Stainless Steels - Duplex

Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa)
- 1A A-743 J93370 .04 1.00 1.00 .04 .04 24.5-26.5 4.75-6.00 1.75-2.25 Cu2.75-3.25 1900°F WQ 100(690) 70(485) 16% 50°F 1900°F WQ 235 typical .280 Duplex stainless steel with Pumps, valve fittings, high
CD4MCu A-890 enhanced mechanical properties, pressure parts, gears, pulp
A-744 corrosion resistance equal to CF-8 and paper equipment
- 4A A-890 J92205 .03 1.5 1.00 .04 .020 21.0-23.5 4.5-6.5 2.5-3.5 Cu1.00 max 2050°F WQ 90(620) 60(415) 25% 50°F 2050°F WQ 235 typical .280 Duplex stainless steel with Pumps, valves, flanges, fittings, and
N.10-.30 enhanced mechanical properties, other pressure containing parts
for corrosive service
Ferralium255® CD4MCuN - J32550 .07 2.00 1.00 .04 .04 24.0-26.5 4.5-6.5 2.9-4.0 Cu 2.0-3.5 2050°F WQ 105(725) 70(485) 20% 50°F 2050°F WQ 235 typical .280 Duplex stainless steel with Pumps, valves, flanges, fittings, and
N.18-.26 enhanced mechanical properties, other pressure containing parts
for corrosive service

Spuncast, Inc. • Tel: 920.261.7853 • E-mail: [email protected] • www.spuncast.com Spuncast, Inc. • Tel: 920.261.7853 • E-mail: [email protected] • www.spuncast.com
 Other Alloys, Special Irons Other Alloys, Special Irons
Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa)
D-2 CD-2 A-597 T90402 1.40-1.60 1.00 1.50 .03 .03 11-13 - .70-1.20 V.40-1.00 1450°F FC - - - Not Usually Welded 688 max .278 Air hardening, high abrasion Processing rolls, tube mill rolls
Co.70-1.00 anneal Rc 60-62 resistance for cold working
both are optional
D-5 CD-5 A-597 T90405 1.35-1.60 .75 1.50 .03 .03 11-13 .40-.60 .70-1.20 V.35-.55 1450°F FC - - - Not Usually Welded 688 max .280 Air hardening like D-2, has 3% Leaf spring forming dies,
optional Co2.50-3.50 anneal Rc 60-62 Co for improved hot hardness hot forming dies
and wear resistance
Ni-RESIST1 Type1 A-436 F41000 3.00 .5-1.5 1.00-2.80 - .12 1.5-2.5 13.50-17.50 - Cu5.50-7.50 1650°F FC 25(172) - - Not Usually Welded 131-183 .282 Wear and corrosion resistant Pump wear rings
anneal iron, good toughness
Ni-RESIST2 Type2 A-436 F41002 3.00 .5-1.5 1.00-2.80 - .12 1.5-2.5 18.00-22.00 - Cu.50 max 1650°F FC 25(172) - - Not Usually Welded 118-174 .278 Wear resistant iron Grinding equipment
anneal
Ductile TypeD2B A-439 F43001 3.00 .70-1.25 1.50-3.00 .08 .02 2.75-4.00 18.00-22.00 - - 1200°F FC stress 58(400) 30(207) 7% Not Usually Welded 139-202 .258-.282 Wear, heat and corrosion resistance Special uses
Ni-Resist relieve,1600°F FC
stabilize,
both optional
HC-250 TypeIIIA A-532 F45009 2.0-3.3 2.0 1.5 .10 .06 23.0-30.0 2.5 max 3.0 max Cu1.2 max 1400°F FC - - - Not Usually Welded 400 .268 Wear resistant white iron Mining, milling, earth handling
anneal alloyed with Cr
Wear resistant white irons - - 1.8-3.6 .25-.8 .5-1.9 .20 .20 - - - - Properties can vary with chemistry, 800-1200°F 1100°F slow 350-500 275-.282 General abrasion resistance Crusher rolls, earth
cooling rate, and heat treatment. slow cool cool optional typical moving equipment
Properties after welding
can vary with
Grey irons, ferritic and pearlitic A-48 - 2.5-4.0 1.0 1.0-3.0 .25 .25 - - - - chemistry, Properties can vary with chemistry, 100-1200°F 1100°F slow 140-270 .246-.267 General engineering use Cylinder liners, rolls
cooling rate, cooling rate, and heat treatment. slow cool cool optional
and heat after welding
Ductile irons, ferritic A-536 - 3.0-4.0 1.0 1.8-2.8 .03 .02 - - - - treatment Properties can vary with chemistry, 800-1200°F 1100°F slow 140-300 .258 High strength, good toughness Pipe, paper mill dryer rolls,
and pearlitic cooling rate, and heat treatment. slow cool cool optional pressure containing parts
after welding
Customer Tollmelt available upon request. Other grades available upon request. Customer Tollmelt available upon request. Other grades available upon request.

Steels: Carbon, Low Alloy, Chrome Steels: Carbon, Low Alloy, Chrome
Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa)
- N-1 A-27 J02500 .25 .75 .80 .03 .03 - - - - 1500°F normalize 60(413) 30(206) 22% 50°F none 183-217 typical .284 Low carbon steel, casting grade General engineering uses
optional
4020 6N A-732 J13512 .35 1.35-1.75 .20-.80 .04 .045 - - .22-.55 - 1750°F NT 90(621) 60(414) 20% 400°F 1750°F NT 183-217 typical .284 High strength quenched and
optional tempered steel
4130 7Q A-732 J13045 .25-.35 .40-.70 .20-.80 .04 .045 .80-1.10 - .15-.25 - 1750°F QT 150(1030) 115(793) 7% 400°F 1750°F QT 255 typical .282 High strength quenched and Hydraulic cylinders, industrial
optional tempered steel machinery, road building equip-
8620 13Q A-732 J12048 .15-.25 .65-.95 .20-.80 .04 .045 .40-.70 .40-.70 .15-.25 - 1650°F QT 105(724) 85(586) 10% 400°F 1650°F QT 197-262 typical .284 High strength quenched and ment, ordinance. Excellent where
optional tempered steel rugged service is required

86B30 SC86B30 - - .32 1.50 .70 .03 .025 .50-.80 .45-.80 .35-.45 B.01 max 1750°F QT 110(757) 94(648) 16% 500°F 1750°F QT 241-262 .282 High strength quenched and
optional typical tempered steel
52100 15A A-732 J19966 .95-1.10 .25-.55 .20-.80 .04 .045 1.30-1.60 - - - 1750°F FC - - - 500°F 1420°F 241 typical .282 High hardness and wear Bearing races
spherodize spherodize annealed resistant steel
anneal anneal
T5 C5 A-217 J42045 .20 .40-.70 .75 .04 .045 4.00-6.50 - .45-.65 - 1650°F NT 90-115 60(415) 18% RA 35% 400°F 1650°F NT 229 typical .280 High strength steel suitable for
(AISI501) temper at (620-795) min temper at 212-440 high temperature service
1250°F min 1250°F min
- Spuncast - - .20 .40-.70 .75 .03 .03 4.00-6.50 - .45-.65 - 1650°F AC 200(1379) 150(1034) 10% 500°F stress relieve at 429-500 typical .280 High strength steel suitable for high Pressure castings, fittings, valves,
C5 450-600°F 400-600°F temperature, service, including high yokes, for service temps not
stress relieve temperature high strength rolls. exceeding 1200°F
T12 C12 A-217 J82090 .20 .35-.65 1.00 .04 .045 8.00-10.00 - .90-1.20 - 1650°F NT 90-115 60(415) 18% RA 35% 400°F 1650°F NT 229 typical .280 High strength steel suitable for high
temper at (620-795) min temper at 212-440 temperature service
1250°F min 1250°F min

Stainless Steels - Precipitation Hardening Stainless Steels - Precipitation Hardening

Similar Spuncast ASTM UNS C Mn Si P S Cr Ni Mo Other PH Heat Tensile Yield Elong.in Weld Weld Brinell Hardness Density Properties Typical Uses
Alloy Alloy Spec max max max max max Treatment (min) (min) 2" min. Preheat Postheat 10mm 3000Kg lbs/in3
KSI(MPa) KSI(MPa)
17-4PH CB7Cu-1 A-747 J92180 .07 .70 1.00 .035 .03 15.50-17.70 3.60-4.60 - (H-900) 170(1170) 170(1170) 5% none or repeat heat 375 min
Cu2.50-3.20 overaged treatment
Cb.15-.35 High strength precipitation
N.05 (H1075) 145(1000) 145(1000) 9% none or repeat heat 277 min Valves, shafts, fuel controls, com-
.280 hardening and good corrosion pressor parts, pulp and paper uses
In H-900 condition overaged treatment and heat resistance
Cb does not apply (H1150) 125(860) 125(860) 10% none or repeat heat 269 min
overaged treatment
15-5PH CB7Cu-2 A-747 J92110 .07 .70 1.00 .035 .03 14.0-15.50 4.50-5.50 - Cu2.50-3.20 Heat treatments Heat treatments and physical properties same as CB7Cu-1
Cb.15-.35 and physical
N.05 properties same
In H-900 condition as CB7Cu-1
Cb does not apply