MASTER PLASTER MPCS-102

(High Performance Additive for plaster, masonry & other cementatious mortars in Manufactured
sand, Crushed Stone Sand or River sand)

Master Plaster MPCS-102 is a highly efficient Adding Master Plaster MPCS-102; 200 ml-800
Plaster, Masonry & Cement Mortar admixture. ml per bag of cement, crushed stone sand, M-
It is a polymer combining powerful plasticizer, Sand can be easily used for plastering, It
powerful waterproofing ingredient, powerful exhibits excellent finish.
binder, anchoring agent and a very powerful
Due to angularity of M-Sand & crushed stone
hygroscopic component.
sand grains, higher interlocking strength and no
Areas of Application crack plaster is feasible when Master Plaster
M-Sand, Crushed stone sand is commonly used MPCS-102 is added to mortar.
for concreting but never used for plastering &
Hygroscopic constitute in Master Plaster
brick masonry. Master Plaster MPCS-102 is
MPCS-102 ensures that sufficient moisture is
compatible with Crush stone sand, m-sand,
available for seamless cement hydration, for
natural sand based plaster, masonry & other
initial period as well as immediately after
cementatious mortars.
plastering hence permitting complete and sound
Its use is approved & consumed by numerous
hydration of cement mortar, leading to firm,
Government departments for application in
tough, waterproof plaster. Hence no shrinkage
plaster, masonry and other cementatious
cracks are seen after initial 24 hours, which
mortars. Its use is ideal for application in
generally appear due to very rapid moisture loss.
 Internal, External & Ceiling plasters of High
Rise Structures & Buildings Advantages

 Masonry Mortars Addition of Master Plaster MPCS-102 in

Crushed stone sand or M-sand plaster mortar
 Cement punning on plaster ensures following advantages:-
1. Improved anchoring properties.
 Plastering water tanks, water retaining walls
2. Throw back material reduces, hence
M-Sand, Crushed stone sand exhibit very high improved economy, greater mason output
rebound; it is very difficult to work with 3. Early setting, after open time, hence
particularly for plastering. However, it is very sufficient strength developed to counter stress
easily available and economical.
leading to crack formation in the initial critical Standards
period of 24 hours. Master Plaster MPCS 102 confirms to IS 1905
4. The plaster is waterproof. Clause 5.4.2 & IS 1661 (reaffirmed 2001)
5. Mortar may be mixed manually or Clause 13 for application of plaster.
mechanically.
Method of Use
6. Not necessary to use dry cement in
Cover all RCC-Masonry joints with appropriate
plastering, hence reduce plastering cost.
mesh and mortar sufficient period prior to
7. The plaster mortar exhibits good
plaster.
workability, hence higher mason output is
For best results, Apply Spatterdash Coat on
observed.
RCC, Cement Blocks, AAC blocks, etc.,
8. Useful for ceiling plaster. Mix Master
surfaces one day prior to plaster. If plastering on
Plaster MPCS-102 in cement slurry which is
un-hacked surface use Razon Anchorex 290
applied on ceiling to be plastered. Reduces
Bonding agent for excellent bonding of mortar
throw back & reduces dry cement
on smooth surfaces.
consumption, increase mason output, ensures
Thoroughly dry mix cement and sand as usual.
high bind strength & good quality
Add Master Plaster MPCS-102 to the gauging
workmanship.
water and add this to the cement-sand mortar.
9. Hygroscopic constituent in Master Plaster
Master Plaster MPCS-102 should never be
MPCS-102 retains sufficient moisture for
added directly to dry mortar. Mix thoroughly.
initial period in Plaster mortar ensuring sound
Use this mortar as usual. Use Master Plaster
seamless hydration, ensuring highest strength
MPCS-102 for internal/external plaster, ceiling
and highest toughness in plaster. Regular water
plaster. When using crushed stone sand plaster,
curing cycle of 10-14 days is essential.
avoid using wooden trowel. Working with
Master Plaster MPCS-102 may be used in smooth surface metallic (aluminum section)
masonry mortar which improves the cohesion of trowels yield best results. Water cure plaster,
the mortar, and eliminates the need to re-fluidize masonry & other cementatious mortars for at
the mortar with water. least 10 to 14 days as usual.
Dosage
Dosage addition of Master Plaster MPCS-102 may vary depending on nature of sand, Type of
cement, ambient temperature and nature of application
Sand MPCS 102 dosage per 50kg bag of cement
River Sand 200 ml – 250 ml, 250 ml for best results
M-Sand or Crushed Stone Sand 400 ml – 800 ml, 500 ml for best results
Washed Sand or Processed Sand 350 ml – 500 ml, 500 ml for best results
Performance
The following results were obtained in a 1:4 Cement & M-Sand mortar using 500 ml Master Plaster
MPCS-102 at 0.65 W/C ratio
S/n Particulars Test Method Result
1. Plastic Density - 2378 kg/m3
2. Initial Flow - 110 mm
3. 3 Days Compressive Strength BS 6319 Pt 2 6.77 N/mm2
4. 28 Days Compressive Strength BS 6319 Pt 2 17.24 N/mm2
5. 28 Days Pull Out Tensile Adhesion Strength ASTM-D 4541 1.20 N/mm2

Product Data
S/n Product Data
1 Colour Brownish Black Liquid
2 Specific Gravity 1.01-1.02 at 25oC
3 pH 6-9
200 ml- 800 ml per 50 kg cement depending on nature of sand,
4 Dosage
cement, ambient temperature and nature of application.
5 Packing 5 Ltr, 20ltr, 50 Ltr.
1 year, store in cool & dry place in a closed container away from
6 Storage/life
direct sunlight.
7 Toxicity & Corrosion Nil. Neither initiates nor promotes corrosion of steel.
For internal , external & ceiling plaster, masonry mortars & other
8 Application cementatious mortars, for plastering buildings, water tanks, water
retaining walls, etc. Compatible with machine applied plaster.
Master Plaster MPCS-102 increases compressive strength
9 Advantages & Tensile Adhesion strengths, imparts waterproofing properties,
improves bonding & prevents cracking.
10 Cement Compatibility OPC, PPC, PSC.
Rev-001 Dated-17/08/2020

It is strongly recommended that site trials be conducted using site conditions and available raw
materials to evaluate the product. Since site materials and conditions are beyond our control and
since above suggestions and recommendations are based on our site trials and laboratory
product evaluation & trials, and since methods of use at site are beyond our control. Hence, no
guarantee can either be implied or enforceable. All Razon datasheets are updated on a regular
basis. It is the user’s responsibility to obtain the latest version.
MANUFACTURER:
RAZON ENGINEERING COMPANY PRIVATE LIMITED
‘Razon House’,660, Taboot Street, P.O.Box No.49, Pune-411001 [India] Ph:91-20-26130791, 26132217
E-mail: [email protected], Website: www.razonengg.com
AN ISO 9001-2015 COMPANY