Product information PI 8/10/06/2023

Long-Life Grease + MoS2

Description

High performance grease for a wide application range

in all motor vehicles and for general machine
lubrication. Thanks to added MoS2 it offers
outstanding protection during extreme loads and high
heat and also adds limp-home properties. For heavily
loaded bearings and joints, splined shafts, threads and
guides. Ideal for constant velocity drive joints.
Certification: DIN 51502 KPF 2K-30. Operating Technical data
temperature range: -65 °C to +120 °C (-86 °F to +248 Four-ball tester wear/indentation 0,8 mm
°F), up to +130 °C (+266 °F) briefly. diameter DIN 51350 part 5

Properties Base oil mineral oil

- friction and wear reducing Viscosity at 104 °F 110,0 mm²/s
- outstanding lubricating action ASTM D 7042-04
- highest load-carrying capacity Flash point 428 °F
- especially resistant to cold and hot water DIN ISO 2592
- economical Pour point -11 °F
- can be delivered by centralized lubrication systems DIN ISO 3016
- universal application
- good corrosion protection
Areas of application
- distinctive high-pressure characteristics
- increases operational reliability
Suitable for a wide application range in all motor
- high resistance to aging
vehicles and for general machine lubrication.

Technical data Comment

Brief description KPF2K-30 WARNING: This product can expose you to
DIN 51502 chemicals including crystalline silica, which is known
Operating temperature range -22 - +266 °F to the State of California to cause cancer. For more
NLGI number 2 information go to www.P65Warnings.ca.gov
DIN 51811
Thickener lithium soap Application
As usual for grease. Follow the instructions of the
Worked penetration 265-295 1/10 mm
bearing manufacturer.
DIN ISO 2137
Dropping point > 356 °F Available pack sizes
DIN ISO 2176
100 g Tube plastic 2003
Color / appearance black USA-AND-CANADA-EN-F
Oil separation after 18 hours at 2,8 % 400 g Cartridge plastic 22255
104 °F DIN 51817 USA-AND-CANADA-EN-F
Oil separation after 7 days at 104 8%
°F DIN 51817 Our information is based on thorough research
Flow pressure at -22 °F < 1400 mbar and may be considered reliable, although not
DIN 51805 legally binding.
Emcor corrosion class 1/1
DIN 51802
Copper corosion after 24 hours at 1b
212 °F DIN 51818
Behavior in the presence of water 0-90
DIN 51807 part 1
Four-ball tester material 2800/3200 N
load/weld force DIN 51350 part 4