KWER 1001-55BR Technical Data Sheet

KWER 1001-55BR is a 55% solid content, aqueous dispersion of modified 1-type solid epoxy

resin. KWER 1001-55BR cured in combination with waterborne curing agent, exhibits good

physical properties as well as water and corrosion resistance for coatings.

Characteristics

. Environmental Friendly (Low VOC)

. Fast dry times & Good adhesion

. High solid

. Long pot life & high gloss

Sales specification
Items Unit KWER 1001-55 TEST method
Viscosity cps at 25℃ 1,000 ~ 15,000 ASTM D 2196
*1
E.E.W g/eq 425 ~ 525 ASTM D 1652
Color - Milky White Visual
N.V wt% 53 ~ 57 KPB-QC2-224
*1 : E.E.W is based on 100 % Solid content
Film Properties
Item Unit Result
Front g x mm 1000 * 500
Impact test
Back g x mm 1000 * 400
flexibility X/X' 3/16’
Cross cut - 100/100
Adhesion (Dolly test) Mpa 8.55
Dry-Hard time hr 2
20º 149
Gloss 60℃ * 1h 60º 152
85º 103
Pencil hardness test 8B - 10H H
Chemical Water 7d Excellent
Resistance NaCl
7d Excellent
(X-cross cutting) (3 wt.% in water)
Sagging mil 12 ↑

25℃ * 1d Haze / Clear Clear

Mixing ratio: KWER 1001-55B/KCA 7700=100/17

Guide formulation
PART A PART B
KWER 1001-55BR (55% solid) 50.1 KCA 7700 9.0
PM (Propylene glycol methyl ether) 3.4
Alkyl(C12-14) glycidyl ether 2.4
Dispersant 2
Deformer 0.05
BaSO4 22
TIO2 6
Talc 5
Carbon black 1.5
DI water 7.1
Thickener 0.3 Mix ratio, vol (A:B) 100 : 9
Wetting agent 0.15 PVC, % 31.7
Total 100 SVR, % 65.0
 Item Unit Result
Front g x mm 1000 * 500
Impact test
Back g x mm 1000 * 300
flexibility X/X' 3/16"
Cross cut - 100/100
Adhesion (Dolly test) Mpa 18.57
Dry-Hard time hr 1.5
20º 66.6
Gloss 60℃ * 1h 60º 82.4
85º 90.3
Sagging mil 12 ↑

Chemical
NaCl
Resistance 7d
(3 wt.% in water)
(X-cross cutting)

Chemical NaCl
7d
Resistance (3 wt.% in water)

Applications

. Waterborne coatings

. Metal coatings

. Industrial Maintenance coatings

. Construction equipment

. Primer coating for new concrete

At temperatures up to 25 °C storage stability packed in original sealed container amounts to at

least 180 days. Store away from excessive heat and humidity.

As a result of the high solids content of the product and the solid resin character of the polymer,

the product tends to form a tiny skin upon foaming and temperature changes during storage.

Therefore filtration of the product (without heating) before applied by the end-user is recommended.

Handling precautions

Reference must be made to the Material Safety Data Sheet (MSDS) for this product.

KER (KWER) is a Kumho P&B Chemicals trade mark

The information contained in this publication is, to the best of our knowledge, true and accurate, but any

recommendations or suggestions which may be made are without guarantee, since the conditions of use are

beyond our control. Furthermore, nothing contained herein shall be construed as a recommendation to use any

product in conflict with existing patents covering any material or its use.