852-1 %)Inspection Certificate 3.

1 According To EN 10204 : 2005

CONSIGNEE Mannat Steel Test Certificate No. : 153326
Date of Issue : 16.09.2021
P. O. No. & Date :
Invoice No. :
Invoice Date :

Supply Process Length Stamp of

Product Grade Tolerance Weight (Mt.)
Condition Route (Meter) Engineer

ASTM A479 EIF-AOD -

Round Bars As Rolled - -
SS 310 CCM

CHEMICAL COMPOSITION (%)

Heat No. C Mn Si S P Cr Ni N Size Pcs
21L0571 0.034 1.64 0.36 0.010 0.034 24.37 19.09 0.0680 20 mm 3
20L1336 0.056 1.61 0.34 0.015 0.036 24.65 19.32 0.0595 40 mm 48
20L0306 0.047 1.66 0.40 0.015 0.037 24.74 19.12 0.0750 16 mm 130
20L1432 0.043 1.74 0.39 0.007 0.033 24.87 19.11 0.0510 18 mm 48
21L0571 0.034 1.64 0.36 0.010 0.034 24.37 19.09 0.0680 22 mm 9

MECHANICAL TEST RESULT / Test Condition : Solution Annealed

Tensile Impact, Joules
Charpy - 2 mm V Notch,
Proof Strength, Strength, Hardness
Elongation Reduction Direction - Longitudinal
Parameter N/MM2 ASTM EN ISO Test Method :- EN ISO 148-1,
% of Area %
A370:17a 6506-1 HBW Test Temperature-
0.2% (Rp 0.2) N/MM2 I II III Average
21L0571/20mm 262 594 57.00 73.40 170-172 - - - -
20L1336/40mm 266 626 55.08 72.04 162-168 - - - -
20L0306/16mm 260 580 55.32 75.22 165-169 - - - -
20L1432/18mm 270 622 56.38 72.04 170-172 - - - -
21L0571/22mm 262 580 56.38 76.10 160-162 - - - -

METALLURGICAL TEST RESULT

JOMINY HARDENABILITY NON METALLIC INCLUSION RATING GRAIN
IS 3848 ASTM E-45 MACRO TEST
SIZE
PARAMETER ASTM
DISTANCE A B C D ASTM
J1 J2 J3 J4 TYPE E 381
MM /INCH T H T H T H T H E 112
RESULT HRC - - - - RESULT - - - - - - - - - -

Remarks:
 Material is ultrasonically tested as per ASTM A388 & found satisfactory.
 The material is free from Radioactive contaminations.
 Lead has not added during manufacturing.
For Laxcon Steels Limited.
We here by certify that above material described herein has been
manufactured and tested with satisfactory results in accordance with
the Specification & requirements
Authorized Signatory (Q.C.)