PRODUCT INFORMATION
PRODUCT DESCRIPTION: XYLAR® 2/E7865A SILVER GRAY
PRODUCT CODE: E7865A
GENERAL INFORMATION:
The primary end use for this coating is: CORROSION RESISTANT PRIMER FOR MARINE
ENVIRONMENTS.
PRODUCT SPECIFICATIONS:
SOLIDS, theoretical: 61.18 ± 3.0% by wt 35.98 ± 3.0% by vol
DENSITY, theoretical: 5.72 ± 0.2 kg/gal 1.51 ± 0.02 kg/liter
COVERAGE, theoretical: 102.52 ft2/kg @ 1 mil 9.51 m2/kg @ 25 microns
586.44 ft2/gal @ 1 mil
VISCOSITY, as shipped: 10 to 20 SECONDS ZAHN #2 (S90) Cup at 77ºF (25ºC)
TYPICAL PROPERTIES:
FLASH POINT: NONE
VOLATILE ORGANIC CMPDS: 0.13 lb/gal 18.00 grams/liter
PREPARATION OF PARTS FOR COATING:
Parts must be free of dirt, oil and other soils to achieve good adhesion and defect free coatings. The
following are the recommended substrates and substrate preparations used with this coating:
SUBSTRATES: COLD ROLLED STEEL, ALUMINUM
SUBSTRATE PREP: DEGREASE AND GRIT BLAST. USE 60-80 MESH ALUMINUM OXIDE
MEDIA FOR GRIT BLAST.
PREPARATION OF COATING MATERIAL:
Mix containers thoroughly by shaking or stirring until any solid material on the bottom has been
eliminated. Best results are obtained when the coating temperature is 65-90ºF (18-32ºC). Adjust
viscosity, if necessary, using the recommended thinner and an accurate Zahn S90 Viscosity Cup. Other
viscosity cups may also be used. Add thinner in increments of 2% until proper viscosity is achieved.
Low viscosity produces runs and sags and low film thickness. High viscosity produces poor sprayability
and uneven appearance. Any dried coating or dirt may be removed by passing the coating through a
100-200 micron filter.
APPLICATION VISCOSITY: AS SUPPLIED, REDUCTION NOT RECOMMENDED
VISCOSITY ADJUSTMENT: DI WATER OR WHITFORD SOLVENT 101 IF NECESSARY.
OTHER INFORMATION: NOTE: WATER WASTE WILL CONTAIN CHROMIUM – MUST DISPOSE
OF PROPERLY
___________________________________________________________________________________________
NON-WARRANTY. The information presented in this publication is based upon the research and experience of Whitford and is to the best of its
knowledge accurate; however, no guarantee of its accuracy is made, Since Whitford has no control over the conditions under which its products
may be employed; and since information as to the physiological and other properties of its products is incomplete, Whitford cannot guarantee
the results obtained and assumes no liability whatsoever for possible damage or injury whether or not caused by following the suggestions in
this brochure. Whitford will not be liable for resulting or consequential damage. Whitford warrants that none of its commercial products infringes
the claims of any United States patent but no license is granted nor recommendation made hereby to practice any invention covered by any
patent owned by Whitford or by others.
PRODUCT INFORMATION Page 2
PRODUCT DESCRIPTION: XYLAR 2/E7865A SILVER GRAY
APPLICATION INFORMATION:
This product is designed primarily for spray application. Consult with a Whitford representative if other
types of application are being considered. Use an air spray gun with a siphon cup or pressure pot.
Select a fluid nozzle and air cap that meet application needs. The Whitford Laboratory uses a Binks
Model 2001 gun with a #66S fluid nozzle and a #66SD air cap. The air supply line must be equipped
with traps to remove water and oil. Drain and service traps frequently.
Apply the dry film thickness as specified. The proper amount of coating should be achieved with two or
three passes of the spray gun across the work piece. Apply the coating to a uniform, full wet
appearance.
DRY FILM THICKNESS: 0.8 TO 1.2 MIL (20 TO 30 MICRONS)
CLEAN UP SOLVENT: WATER, CLEAN EQUIPMENT IMMEDIATELY, DO NOT ALLOW TO DRY.
CURING THE COATING:
In order to completely cure the coating, the SUBSTRATE TEMPERATURE must remain at the specified
temperature for the entire bake schedule.
FLASH OR AIR DRY: AMBIENT TO 150°F (66°C) UNTIL PART TURNS COMPLETELY GRAY
BAKE SCHEDULE: 5 - 10 MINUTES @ 750-650°F (400-343°C)
TYPICAL CURED FILM PROPERTIES:
Evaluate the coating according to the following specifications:
PENCIL HARDNESS: >8H GLOSS: MATT AS SPRAYED
CURE TEST: WHITFORD TM-115C/ APPLY 1 DROP HOT WATER TO PART. LET
STAND 1 MINUTE, BLOT WITH PAPER TOWEL = NO DISCOLORATION
ON TOWEL.
ADHESION: EXCELLENT KNIFE SCRATCH ADHESION.
OTHER: MATERIAL CAN BE BURNISHED FOR BETTER CORROSION
RESISTANCE AND APPEARANCE.
HANDLING & STORAGE:
Keep containers tightly closed when not in use. Store between 40 to 95ºF (4 to 35ºC). Avoid breathing
fumes during application or curing. Wash hands thoroughly before smoking or eating. Wear appropriate
protective equipment while handling.
SHELF LIFE: 6 MONTHS (MIX 30-60 MINUTES MONTHLY TO MAINTAIN QUALITY).
PREPARED BY: SEM UPDATED: 25 JULY 2017
___________________________________________________________________________________________
NON-WARRANTY. The information presented in this publication is based upon the research and experience of Whitford and is to the best of its
knowledge accurate; however, no guarantee of its accuracy is made, Since Whitford has no control over the conditions under which its products
may be employed; and since information as to the physiological and other properties of its products is incomplete, Whitford cannot guarantee
the results obtained and assumes no liability whatsoever for possible damage or injury whether or not caused by following the suggestions in
this brochure. Whitford will not be liable for resulting or consequential damage. Whitford warrants that none of its commercial products infringes
the claims of any United States patent but no license is granted nor recommendation made hereby to practice any invention covered by any
patent owned by Whitford or by others.