Technical data
Physical Nominal Value Unit Test Method
Density (23°C) 1.175 g/cm³ ISO 1183
Melt Mass-Flow Rate ISO 1133
17.2 g/10 min
(MFR) (330°C/2.16 kg)
Melt Volume-Flow Rate ISO 1133
17.2 cm³/10min
(MVR) (330°C/2.16 kg)
Molding Shrinkage 3 ISO 294-4
Across Flow : 2.00
0.81 %
mm
Flow : 2.00 mm 0.81 %
Water Absorption ISO 62
Saturation, 23°C 0.33 %
Equilibrium, 23°C,
0.13 %
50% RH
Hardness Nominal Value Unit Test Method
Ball Indentation Hardness 125 MPa ISO 2039-1
Mechanical Nominal Value Unit Test Method
Tensile Modulus (23°C) 2430 MPa ISO 527-2/1
Tensile Stress (Yield, 23° 72 MPa ISO 527-2/50
Tensile Strain (Yield, 23° 6.83 % ISO 527-2/50
Nominal Tensile Strain at ISO 527-2/50
> 48 %
Break (23°C)
Flexural Modulus 4 (23°C) 2430 MPa ISO 178
Flexural Stress 4 (23°C) 102 MPa ISO 178
Impact Nominal Value Unit Test Method
Charpy Unnotched ISO 179/1eU
Impact Strength
-30°C No Break
23°C No Break
Thermal Nominal Value Unit Test Method
Heat Deflection
Temperature
0.45 MPa, 158 °C ISO 75-2/B
1.8 MPa, Unannealed 141 °C ISO 75-2/A
Vicat Softening ISO 306/B120
171 °C
Temperature
CLTE ISO 11359-2
Flow : 23 to 55°C 6.50E-05 cm/cm/°C
Transverse : 23 to 55°
6.50E-05 cm/cm/°C
C
RTI Elec 141 °C UL 746
RTI Imp 132 °C UL 746
RTI Str 141 °C UL 746
Electrical Nominal Value Unit Test Method
Surface Resistivity 1.00E+16 ohms IEC 60093
Volume Resistivity (23°C) 1.00E+17 ohms·cm IEC 60093
Electric Strength (23°C, IEC 60243-1
35 kV/mm
1.00 mm)
Relative Permittivity IEC 60250
23°C, 100 Hz 3
23°C, 1 MHz 2.9
Dissipation Factor IEC 60250
23°C, 100 Hz 1.00E-03
23°C, 1 MHz 8.00E-03
Comparative Tracking IEC 60112
Index
Solution A 250 V
Solution B 125 V
Flammability Nominal Value Unit Test Method
UL 94
Flame Rating (1.5 mm) HB
Glow Wire Flammability IEC 60695-2-12
855 °C
Index
Oxygen Index 5 25 % ISO 4589-2
Optical Nominal Value Unit Test Method
Refractive Index 6 1.578 ISO 489
Transmittance (1000 µm) 88 % ISO 13468-2
Additional Information Nominal Value Test Method
Electrolytical Corrosion IEC 60426
A1
(23°C)
Injection Nominal Value Unit
Drying Temperature - Dry
135 °C
Air Dryer
Drying Time - Dry Air
2.0 to 4.0 hr
Dryer
Suggested Max Moisture < 0.020 %
Suggested Shot Size 30 to 70 %
Rear Temperature 310 to 320 °C
Middle Temperature 315 to 325 °C
Front Temperature 315 to 330 °C
Nozzle Temperature 310 to 335 °C
Processing (Melt) Temp 320 to 340 °C
Mold Temperature 90 to 130 °C
Back Pressure 10.0 to 20.0 MPa
Vent Depth 0.025 to 0.050 mm
Injection Notes
Standard Melt Temperature: 330°C
Peripheral Screw Speed: 0.05 - 0.2 m/s
Hold Pressure (% of Injection Pressure): 50 - 75%