Product Information
Oct 2019
Ultraform® W 2320 003 AT
Polyoxymethylene (POM)
Product Description
Ultraform W 2320 003 AT is a very easy flowing and rapidly solidifying injection molding POM grade
for use where processing is extremely difficult but mechanical properties are lower. Contains a mold
release agent.
Applications
Typical applications include thin walled parts.
PHYSICAL ISO Test Method Property Value
Density, g/cm³ 1183 1.41
Mold Shrinkage, parallel, % 294-4 2
Mold Shrinkage, normal, % 294-4 2.1
Moisture, % 62
(50% RH) 0.2
(Saturation) 0.8
RHEOLOGICAL ISO Test Method Property Value
Melt Volume Rate (190 C/2.16 Kg), cc/10min. 1133 25
MECHANICAL ISO Test Method Property Value
Tensile Modulus, MPa 527
23C 2,850
Tensile stress at yield, MPa 527
23C 65
Tensile strain at yield, % 527
23C 8
Nominal strain at break, % 527
23C 24
IMPACT ISO Test Method Property Value
Izod Notched Impact, kJ/m2 180
-30C 5
23C 5
Charpy Notched, kJ/m2 179
-30C 4
23C 4.5
Charpy Unnotched, kJ/m2 179
-30C 190
23C 190
THERMAL ISO Test Method Property Value
Melting Point, C 3146 166
HDT A, C 75 100
Coef. of Linear Thermal Expansion, Parallel, 1.1 X10-4
mm/mm C
ELECTRICAL ISO Test Method Property Value
Comparative Tracking Index IEC 60112 600
BASF Corporation General Information: 800-BC-RESIN
Engineering Plastics Technical Assistance: 800-527-TECH (734-324-5150)
1609 Biddle Avenue Web address: http://www.plasticsportal.com/usa
Wyandotte, MI 48192 Page 1 of 3
Ultraform® W 2320 003 AT
Volume Resistivity (Ohm-m) IEC 60093 1E11
Surface Resistivity (Ohm) IEC 60093 1E13
Dielectric Constant (1 MHz) IEC 60250 3.8
Dissipation Factor (1 MHz), E-4 IEC 60250 50
UL RATINGS UL Test Method Property Value
Flammability Rating, 0.75mm UL94 HB
Relative Temperature Index, 0.75mm UL746B
Electrical, C 105
Flammability Rating, 1.5mm UL94 HB
Relative Temperature Index, 1.5mm UL746B
Mechanical w/o Impact, C 90
Mechanical w/ Impact, C 90
Electrical, C 105
Flammability Rating, 3.0mm UL94 HB
Relative Temperature Index, 3.0mm UL746B
Mechanical w/o Impact, C 105
Mechanical w/ Impact, C 90
Electrical, C 105
Processing Guidelines
Material Handling
Max. Water content: 0.15%
Product is supplied in polyethylene bags and drying prior to molding is not required. However, after
relatively long storage or when handling material from previously opened containers, preliminary
drying is recommended in order to remove any moisture which has been absorbed. If drying is
required, a dehumidifying or desiccant dryer operating at 80 - 110C (176 - 230F) is recommended.
Drying time is dependent on moisture level, however 2-4 hours is generally sufficient. Further
information concerning safe handling prCedures can be obtained from the Safety Data Sheet.
Alternatively, please contact your BASF representative.
Typical Profile
Melt Temperature 190-230C (375-446F)
Mold Temperature 60-120C (140-248F)
Injection and Packing Pressure 35-70 bar (500-1000psi)
Mold Temperatures
A mold temperature of 80-90C (176-194F) is recommended, however temperatures of as low as
45C (113F) and as high as 105C (221F) can be used where applicable.
Pressures
Injection speed must be optimized. A filling rate which is too high results in anisotropic mechanical
properties, while a filling rate which is too low yields parts with poor surface finish. The tool must be
vented to avoid burn marks and prevent mold deposits. Injection pressure controls the filling of the
part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be
used effectively in controlling sink marks and shrinkage. It should be applied and maintained until
the gate area is completely frozen off.
Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas.
Fill Rate
Injection speed must be optimized. A filling rate which is too high results in anisotropic mechanical
properties, while a filling rate which is too low yields parts with poor surface finish. The tool must be
vented to avoid burn marks and prevent mold deposits.
BASF Corporation General Information: 800-BC-RESIN
Engineering Plastics Technical Assistance: 800-527-TECH (734-324-5150)
1609 Biddle Avenue Web address: http://www.plasticsportal.com/usa
Wyandotte, MI 48192 Page 2 of 3
Ultraform® W 2320 003 AT
Note
Although all statements and information in this publication are believed to be accurate and reliable,
they are presented gratis and for guidance only, and risks and liability for results obtained by use of
the products or application of the suggestions described are assumed by the user. NO
WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OF
MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING
PRODUCTS DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH. Statements or
suggestions concerning possible use of the products are made without representation or warranty
that any such use is free of patent infringement and are not recommendations to infringe any
patent. The user should not assume that toxicity data and safety measures are indicated or that
other measures may not be required.
BASF Corporation General Information: 800-BC-RESIN
Engineering Plastics Technical Assistance: 800-527-TECH (734-324-5150)
1609 Biddle Avenue Web address: http://www.plasticsportal.com/usa
Wyandotte, MI 48192 Page 3 of 3