IRJET- Effect on M30 SCBA Concrete in Acidic Environment

International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 12 | Dec 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1140
EFFECT ON M30 SCBA CONCRETE IN ACIDIC ENVIRONMENT
P. V. RamBabu¹, V. Jahnavi Deepthi², G. V. Ramarao³
¹Assistant Professor, Department of Civil Engineering, S.R.K.R. Engineering College, Bhimavaram,
Andhra Pradesh, India.
²P.G. Student, Department of Civil engineering, S.R.K.R. Engineering college, Bhimavaram, Andhra Pradesh, India.
³Professor, Department of Civil Engineering, Andhra University, Vishakhapatnam, Andhra Pradesh, India.
----------------------------------------------------------------------***---------------------------------------------------------------------
ABSTRACT - Theusageofblendedconcretebecomingpopular
due to the less usage of cement, at the same time the disposal
issue of industrial and agriculturalwastescanalsobereduced.
In this experiment we analyze the impact of partial
replacement of SCBA in ordinary Portland cement cured in
various acidic environments. Bagasseashhasbeenreplacedby
0%, 5%, 10%, 15% and 20% by weight of cement. The
concrete specimens were cured for 28, 60and90daysin water
and in concentrations of 1%, 3 % and 5% sulphuric acid and
hydrochloric acid solutions. The tests conducted are
compressive strength. The ideal percentage of SCBA
replacement is around 10%. The presence of SCBA in concrete
developed resistivity towards Acidic attacks.
KEY WORDS: Compressive strength, durability, sugar cane
bagasse ash, hydro chloric acid (HCL) and sulphuric acid
(H₂SO₄).
1. INTRODUCTION:
In present situation all over the world are seeking on
utilization of industrial waste in useful manner, by avoiding
disposal problems and landfilling cost [1]. Utilization of
various supplementary cementitious materials significantly
influences fresh and hardened properties of mortar.
Sugarcane bagasse ash is a by-product fromsugarindustries
and can be used as supplementary cementitious material in
concrete [2, 3]. When this waste is burned under controlled
conditions, it also gives ash having amorphous silica, which
has pozzolanic properties. A few studies have been carried
out on the ashes obtained directly from the industries to
study pozzolanic activity and their suitability as binders,
partially replacing cement [4]. Lakshmi Priya [5]
investigated the impact of SCBA in concrete by partially
replacing SCBA with cement in the ratio of 0%, 5%, 10%,
15%, 20% and 25% by weight for M25 grade of concrete.
The experimental study examined the slump of the fresh
concrete, compaction factor, compressive strength, split
tensile strength, flexural strength, and modulus of elasticity.
Vijaya Sehkar Reddy [7] conducted a study where the
replacement is done at various percentages like 0%, 5%,
10%, 15% and 20% and its effect on properties of concrete
was investigated.. Fresh and hardened properties were
exercised with various replacement levels. The study
indicated that sugarcane bagasse ash can effectively be used
as cement replacement (up to 10%) without substantial
change in strength.
Here, we used the sugar cane bagasse ash as a replacement
by 0%, 5%, 10%, 15% and 20% by weight of cement
improve quality and reduce the construction cost on
materials. The concrete specimenswerecuredfor28,60and
90 days in water and in concentrations of 1%, 3 % and 5%
sulphuric acid and hydrochloric acid solutions. The tests
conducted are compressive strength. The main objective of
this research is to study the durability of sugar cane bagasse
ash blended concrete cured in H₂SO4and HCL solution.
2. METHODOLOGY
The materials used in this investigation are:
2.1. Cement: The most commonly used cement in concrete
is ordinary Portland cement of 53 Grade confirming IS
12600- 1989 (2009).
2.2. Fine aggregate: Regionally available river sand,
confirming to Zone II as per Indian standards 383-2016.The
sand used must be free from clay, silt and other organic
impurities. Specific gravity is about 2.6, water absorption is
1% and fineness modulus is around 2.99.
2.3.Coarse aggregate: The crushed aggregate used were
20mm to 12.5mm in size confirming to IS: 10262, IS: 383.
Specific gravity is 2.8, water absorption is 0.5% andfineness
modulus is 7.26.
2.4. Water: The water that is availableinourcollegecampus
confirming to the requirement of concreting and curing as
per IS: 456-2009.
2.5. Sugar cane bagasse ash: TheSCBAwhichisusedinthis
investigation process was obtained from the KCP Sugar
factory, Vuyurru,locatedin Krishna district,Andhra Pradesh.
SCBA contains an approximate 25% of hemi-cellulose,about
25% of lignin and a 50% of cellulose. For each ton of the
sugarcane it generates approximately 26% of bagasse at an
approximate 50% of moisture content & approximately
0.62% of residual ash. The residue that is left after the
combustion gives a chemical composition which is highly
dominated by silicon dioxide (SO2). The specific gravity of
SCBA was found to be 2.49

Table-1: Physical properties of sugar cane bagasse ash
S. No Property Test Results
1 Specific gravity 2.49
2 Particle shape Spherical
3 Density 375 Kg/m³
4 Specific surface area 420/Kg
3. EXPERIMENTAL PROCEDURE
3.1. Mixing
Mixing is done in a pan mixer of 40 liters capacity. The
cement materials are thoroughly blended and then to this,
the aggregates were added and then completely mixed
followed by the slow and gradual addition of water. The
mixing has to be done properly until a mixture of uniform
colour and consistency are achieved which is ready for
casting.
3.2. Casting of specimen
The moulds are cleaned and oil is applied to the mould
before concrete is poured into the mould. The moulds are
then placed on the level platform. The thoroughly mixed
green concrete is filled into the moulds by a vibration
method with needle vibrator. Excess concrete was removed
and top surface is leveled confirming to IS: 516-1969. Here
number of cubes cast are 315, number of cylinders cast are
315 and number of beams cast are 315.
3.3. Curing the specimen
The specimens in the mould are left undisturbed for 24
hours in moulds and then de moulded. De moldings must be
done carefully without breaking edges. They must be cured
in water, H₂SO4 and HCL solutions for required period
confirming to IS: 516-1969.
3.4. Durability
The durability tests are conducted on sugarcanebagasse ash
concrete against acids such as H₂SO4and HCL. The response
of H₂SO4 and HCL attack on sugar cane bagasse ash concrete
for various percentages were studied. For conducting this
tests concrete specimens like cubes, cylinders and beams
with different percentages were casted.Thespecimenswere
cured in 1%, 3% and 5% H₂SO4and HCL solutions for
different periods of 28, 60 and 90 days.
4. EXPERIMENTAL RESULTS
The following graphs shows the mechanical properties of
concrete specimens with 0%, 5%, 10%, 15% and 20%
weight replacement of cement with SCBA cured in normal
water and different percentages of H₂So₄ and HCL solutions
for 28, 60 and 90 days.
4.1. Compressive strength results for cubes cured in
water
Chart-1: CS of SCBA cubes cured in normal water
The obtained results of SCBA replaced concrete cubes cured
in water of all curing periods, the strength variation for 0%
to 5% increased up to 2.99% for 28 days, 1.14% for 60 days,
2.3% for 90 days. For 5% to 10% strength increased up to
2.33% for 28 days, 2.81% for 60 days and 2.68%for90days.
For 10% to 15% strength decreasedupto9.22%for28days,
5.47% for 60 days, 7.49% for 90 days and for 15% to 20%
strength decreased up to 2.95% for 28 days, 2.4% for 60
days, 2.82% for 90 days. This shows that compressive
strength results of SCBA replaced concrete cubes cured in
water for all curing periods increase up to 10% replacement
and a decrease in compressive strength is observed at 15%
and 20% replacements.
4.2. Compressive strength results for cubes cured in 1%
HCL solution
Chart-2: CS of SCBA cubes cured in 1% HCL solution
in 1%HCL of all curing periods, the strengthvariationfor 0%
to 5% strength increased up to 4.38% for 28 days, 3.23%for
60 days and 8.7% for 90 days. For 5% to 10% strength
increased up to 2.7% for 28 days, 2.4%for 60 days and 9.2%
for 90 days. For 10% to 15% strengthdecreasedupto10.4%
for 28 days, 14.09% for 60 days and 28.1% for 90 days and
for 15% to 20% strength decreased up to 12.9% for 28days,
12.6% for 60 days and 7.1% for 90 days. This shows that
compressive strength results of SCBA replaced concrete
cubes cured in 1%HCL for all curing periods increase up to
10% replacement and a decrease in compressive strength is
observed at 15% and 20% replacements.

HCL solution
to 5% strength increased up to 7.04% for 28 days, 5.8% for
increased up to 4.99% for 28 days, 4.93% for 60 days and
2.47% 90 days, for 10% to 15% strength decreased up to
20.9% for 28 days, 22.77% for 60 days and 26.17% for 90
days and for 15% to 20% strengthdecreasedupto16.7% for
28 days, 21.47% for 60 days and 1.67% for 90 days. This
shows that compressive strength results of SCBA replaced
concrete cubes cured in 3% HCL for all curing periods
increase up to 10% replacement and a decrease in
compressive strength is observed at 15% and 20%
replacements.
HCL solution
to 5% strength increased up to 4.12% for 28 days, 8.5% for
increased up to 4.7% for 28 days, 4.4% for 60 days and4.6%
for 90 days. For 10% to 15% strengthdecreasedupto22.3%
for 28 days, 28.07% for 60 days and 29.2% for 90 days and
for 15% to 20% strength decreased up to 24.6% for 28days,
18.5% for 60 days and 20.88% for 90 days. This shows that
cubes cured in 5% HCL for all curing periods increase up to
H₂So₄ solution
Chart-5: CS of SCBA cubes cured in 1% H₂So₄ solution
The obtained results of SCBA replaced concretecubescured
in 1% H₂So4 of all curing periods, the strength variation for
0% to 5% strength increased up to 4.13%for28days,6.47%
foe 60 days, 19.94% for 90 days. For 5% to 10% strength
6% for 90 days. For 10% to 15% strength decreased up to
13.72% for 28 days, 12.23% for 60 days, 24.69% for 90days
and for 15% to 20% strength decreased up to 9.95% for 28
days, 13.17% for 60 days, 7.97% for90days.Thisshowsthat
cubes cured in 1% H₂So4 for all curing periodsincreaseupto
H₂So₄ solution
for 60 days, 19.12% for 90 days, for 5% to 10% strength
4.04% for 90 days, for 10% to 15% strength decreased up to
21% for 28 days, 22.89% for 60 days, 26.67% for 90 days
and for 15% to 20% strength decreased up to 8.28% for 28
days, 13.51% for 60 days, 12.84 % for 90 days. This shows
that compressive strength of SCBA replaced concrete cubes

cured in 3% H₂So4 for all curing periods increase up to 10%
replacement and a decrease in compressive strength is
H₂So₄ solution
for 60 days, 9% for 90 days. For 5% to 10% strength
13.57% for 90 days. For 10% to 15% strength decreased up
to 27.75% for 28 days, 31.35% for 60 days, 21.16% for 90
days and for 15% to 20% strength decreased up to 13.07%
for 28 days, 4.67% for 60 days, 18.26% for 90 days. This
shows that compressive strength of SCBA replaced concrete
cubes cured in 5% H₂So4 for all curing periodsincreaseupto
5. CONCLUSIONS
 It was observed that due to the presence of high
amount of silica in SCBA, the concrete blended with
10% SCBA by weight of cement has more strength
when compared to ordinary concrete in all curing
conditions.
 There is a decrease in strength and increase in
slump after addition of SCBA beyond 10% SCBA
replacement by weight of cement.
 The strength increased in SCBA concretespecimens
cured in 1% hydrochloric acid and sulphuric acid
solution when compared with specimens cured in
normal concrete at 90 days.
 SCBA replaced concrete specimens produced
maximum compressivestrengthwhencuredin both
sulphuric acid and Hydrochloric acid when
compared with normal concrete.
 The presence of SCBA in concrete developed
resistivity towards Acidic attack.
6. REFERENCES
1. Akash G S, Madhukar K, Chetan T, Aishwarya T, Dinesh S
Magnur, Dr. Sivakumar B, “Experimental Study On Partial
Replacement Of Sand With Sugarcane Bagasse Ash In
Concrete”, International ResearchJournal ofEngineering and
Technology (IRJET), Volume: 05 Issue: 5, May-2018.
2. Alireza Joshaghani, Ali Akbar Ramezanianpour, Hossein
Rostami, “Effect of incorporating Sugarcane Bagasse Ash
(SCBA) in mortar to examine durability of sulphate attack”,
ResearchGate, Conference Paper· June 2016
3. BangarSayali S, PhalkeShubhangi N, Gawade Anjali Y,
Tambe Rutuja S and Rahane A. B, “A Review Paper On
Replacement Of Cement With Bagasse Ash”, International
Journal Of Engineering Sciences and Management, March
2017
4. Jayminkumar A. Patel, D. B.Raijiwala,“Experimental Study
on Use of Sugar Cane Bagasse Ash in Concrete by Partially
Replacement with Cement”, International Journal of
Innovative ResearchinScience,Engineeringand Technology,
Vol. 4, Issue 4, April 2015.
5. K. Lakshmi Priya, R. Ragupathy, “Effect of Sugarcane
Bagasse Ash on Strength Properties of Concrete”,
International Journal of Research in Engineering and
Technology (IJRET), 2016, Vol. 05, No. 04, pp. 159-164.
6. Khansaheb A. P, “Experimental InvestigationonProperties
of Concrete Using Human Hair & Sugarcane Bagasse Ash”,
International Journal of Innovative and Emerging Research
in Engineering Volume 2, Issue 5, 2015
7. M. Vijaya Sekhar Reddy, K. Ashalatha, M. Madhuri, P.
Sumalatha, “Utilization of Sugarcane Bagasse Ash (SCBA) In
Concrete By partial Replacement Of Cement”, International
Organization of Scientific Research Journal of Mechanical
and Civil Engineering (IOSR-JMCE), 2015, Vol. 12, No.06, pp.
12-16.
8. M. S. Chennakesava Rao, N. V. N. Prabath, “Green Concrete
using Agro Industrial Waste (Sugarcane Bagasse ASH)”,
International Journal of Soft Computing and Engineering
(IJSCE)ISSN: 2231-2307, Volume-5 Issue-1, March 2015
9. P V Rambabu, G. Aditya, G V Ramarao, “Effect of Acidic
Environment (HCL) on Concrete With Sugarcane Bagasse
Ash As Pozzolana”, International Journal of Engineering
Research and Applications (ijera)ISSN: 2248-9622, Vol. 5,
Issue 11, (Part - 4) November 2015, pp.59-64
10. T. S. Abdulkadir, D. O. Oyejobi, A. A. Lawal, “Evaluation
of sugercane bagasse ash as a replacement for cement in
concrete works”,ACTATEHNICACORVINIENSIS – Bulletinof
Engineering, Tome VII, Fascicule 3, September 2014.

11. T. Subramani, M. Prabhakaran, “Experimental Study On
Bagasse Ash In Concrete”, International Journal of
Application or Innovation in Engineering & Management
(IJAIEM), Volume 4, Issue 5, May 2015
12. U.R.Kawade1, Mr.V.R.Rathi2, Miss Vaishali D. Girge,
“Effect of use of Bagasse Ash on Strength of Concrete”,
International Journal of Innovative Research in Science,
Engineering and Technology Vol. 2, Issue 7, July 2013

IRJET- Effect on M30 SCBA Concrete in Acidic Environment

More Related Content

What's hot

Similar to IRJET- Effect on M30 SCBA Concrete in Acidic Environment

More from IRJET Journal

Recently uploaded

IRJET- Effect on M30 SCBA Concrete in Acidic Environment