Ceraboard
TYPE Description
Rigid panel based on refractory fibres.
Ceraboard is a refractory fibre board supplied in
CLASSIFICATION TEMPERATURE & panels of standard thicknesses made from a
GRADES VAILABLE slurry of refractory fibres and binders which
Ceraboard 100 : 1260°C have a low organic content.
Ceraboard 115 : 1400°C
The maximum continuous use temperature The combination of different refractory fibres,
depends on the application. In case of doubt, refer inorganic and organic binders in different
to your local Morgan Thermal Ceramics distributor proportions allows types of boards to be made
for advice. suitable for different use temperatures.
In some types of heating equipment the
THICKNESS TOLERANCES emission of fumes, which can occur when
binders burn out of the board, can be easily
Less than 10mm: +/- 0.5mm (except for eliminated.
Ceraboard 100: +/- 1mm)
From 10mm to 20mm: +/- 1mm FEATURES
From 25mm to 50mm: +/- 2mm
High temperature stability
More than 50mm: +/- 4mm
Low thermal conductivity
Low heat storage
Rigidity and high cohesive strength allow
machiningand cutting
Resistant to thermal shock
Good erosion resistance
Can be used in direct contact with flame
Easy application
APPLICATIONS
These versatile boards can be used where a
rigid, self-supporting and insulating product is
required which also has good resistance to
physical damage.
Ceramic industry (kiln linings & kiln car
insulation)
Glass industry
Ducts insulation
General thermal barriers
High temperature insulation
[Link]
Europe: +44 (0) 151 334 4030 / [Link]@[Link]
North America: +1 (0) 706 796 4200 / [Link]@[Link]
South America: +54 (11) 4373 4439 / [Link]@[Link]
Asia: +65 (0) 6595 0000 / [Link]@[Link]
Ceraboard
Classification temperature 100 115
°C 1260 1400
Properties Measured at Ambient Conditions
(23°C/50 % RH)
Colour White/ tan White/ tan
Density Kg/m3 310** 310
Modulus of rupture 1.0** 0.9
MPa
Compressive stress at 10% relative deformation 0.35 0.3
MPa
High Temperature Performance*
Loss of ignition after 2 hours heating at 800°C 5.5 3.5
%
Permanent linear shrinkage (ASTM C-356) after 24 3.0 3.7
hours isothermal heating at classification temperature:
%
Thermal conductivity (ATM-201) at mean temperature
of
300°C W/m.K 0.07 0.07
400°C W/m.K 0.08 0.08
600°C W/m.K 0.11 0.11
800°C W/m.K 0.15 0.15
1000°C W/m.K 0.20 0.20
* Values for thickness 50mm. ** Values 330 and 1.5 for thicknesses below 20mm.
[Link]
Europe: +44 (0) 151 334 4030 / [Link]@[Link]
North America: +1 (0) 706 796 4200 / [Link]@[Link]
South America: +54 (11) 4373 4439 / [Link]@[Link]
Asia: +65 (0) 6595 0000 / [Link]@[Link]
Ceraboard
Availability and Packaging
Standard Dimensions Ceraboard 100 Ceraboard 115
mm
Board per Board per
carton pallet carton pallet
1200 x 1000 x 6 20 160
1200 x 1000 x 7.5 16 120
1200 x 1000 x 10 12 90
1200 x 1000 x 13 10 72
1200 x 1000 x 15 8 60
1200 x 1000 x 20 6 48
1200 x 1000 x 25 5 36 5 36
1200 x 1000 x 40 3 24 3 24
1200 x 1000 x 50 2 18 2 18
Ceraboard is packed in cartons or on pallets which are shrink wrapped with recyclable plastic.
The values given herein are typical values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical
service and are subject to change without notice. Therefore, the data contained herein should not be used for specification purposes. Check with your Thermal Ceramics office to obtain
current information.
[Link]
Europe: +44 (0) 151 334 4030 / [Link]@[Link]
North America: +1 (0) 706 796 4200 / [Link]@[Link]
South America: +54 (11) 4373 4439 / [Link]@[Link]
Asia: +65 (0) 6595 0000 / [Link]@[Link]