[POLYSTAR UG-850]

Gel-coat Resin
1. Type
6. Caution Rules at Hardening
Non-Promoted, Non-Waxed, Vinylester
- The Gel-time is a change working conditions
type Gel-coat resin.
(ex. temperature, humidity). Please adjust
amount of hardener & promoter according to
2. Use working conditions, before use.
POLYSTAR UG-850 is vinylester type Gel-coat Resin -The hardener amount is appropriate 1% of
Which is designed for the production of mold. resin for suitable hardening.
- As hardening can be delayed according to
work temperature, you should use it in proper
3. Distinguishing Characteristics temperature.
-. Good heat resistance
-. Good solvent resistance. 7. Caution Rules at Use
-. Good boiling water resistance. - Keep it at the place that can cut off heat,
light. Please pay attention to firearms.
* Good impact resistance. - As a hardener can explode, Please keep it at
the place that can avoid the heat, a shock, A
4. Typical Properties:Liquid Resins *1
direct sunlight.
Units Spec Remarks - If hardener and promoter come directly in
contact, they can explode. You should not
Viscosity Poise/25℃ 17 – 25 #4, 60 rpm
keep together at all it.
Thixotropic - Put on gloves and a mask when you work.
- 4.0 – 4.5 6/60 rpm
Index - Ventilate a workplace at any time.
6%Co-N 0.5 phr
Gel-time Min 18 - 27 - After use, residual resin should seal.
MEKPO 1.0 phr
(Water, dust get into the resin or Styrene
at 25℃ monomer evaporates, and the resin can be
*1. Values are representative. degenerated.)
Specification limits are available upon request. - Styrene uses below 3percents in order to
adjust viscosity.
[Link] Properties: Cured Resin *2 - Please use the amount that use is possible
only within work time.
Unit Results Remarks
- If the resin or a hardener get into worker’s
Tensile Strength MPa 70 ASTM D 638 eyes, Please wash eyes immediately more
Elongation
% 3.5 than 15 minutes with running water and get
from prescription of a doctor.
Flexural Strength MPa 90 ASTM D 790
-Do not leave the Resin at the place of direct
Flexural Modulus GPa 3.5 sunlight or heat.
Barcol Hardness - 42 ASTM D 2583

Heat Distortion Temp. ℃ 115 ASTM D 648

Water absorption % 0.1 ASTM D 570

*2. Thickness : 3 mm
Promoter : 6% Co-N 1.0 phr
Catalyst : 55% MEKPO 1.0 phr
Post Cure : 25C 6hrs, 80C 4hrs

169, Taehwa-Dong, Daeduk-Gu, Taejon, R.O Korea TEL)042-625-2541 FAX)042-634-7543

. For more information regarding safe & health, please refer MSDS providing in our companies.
The company cannot accept liability for use the technical data for anything other than reference.