FOR CRUSHER PLATE
Chemical composition (%) Mechanical Properties Area of Application
C Si Mn P S Cr Mo Ni Elongation Tensile Hardness General Application Remarks
Material (%) Strength (BHN)
(Mpa)
Grade 1.05- 1.0 11.0 0.08 0.025 - - - 24 (min) 600 (min) 229 In general, manganese Work hardening
-1 1.35 - (max) steels will be used done at slower
14.0 whenever very high rate but wear
shock resistance or resistance is better
some elongation is
needed. This alloy is
Grade 1.05- 1.0 11.0 0.08 0.025 1.5- - - 24(min) 600 (min) 229 used for crushing less Work hardening
-3 1.35 - 2.5 (max) abrasive and very large done at slower
Austenitic 14.0 feed material (e.g. rate but wear
Manganese limestone). resistance is better
Steel
Grade 1.05- 0.30- 16.0 0.08 0.025 1.5- - - - - 280 Work Hardening
-7 1.35 0.90 - 2.5 (max) done at 20-25%
19.0 Faster rate but less
wear resistant than
12-14% Austenitic
Manganese steel
Advantage over the Austenitic Disadvantage over the Mechanical Composition
Manganese steel Austenitic Manganese steel Elongation Tensile Hardness
Material (%)
Area of Application
Strength (BHN)
(Mpa)
Martensitic martensitic steels have a Feed size is limited to 900 18 620-795 240 Martensitic steel will be used whenever hardness
(Alloy) Steels higher lifetime than mm. and impact resistance are both needed. It is used
(CA15 – Eq. to manganese steels in more in primary and recycling applications.
AISI 410) abrasive applications when the
feed size is below 900 mm. It
can tolerate steel in the feed
material
Chemical composition (%) Mechanical Properties
C Si Mn P S Cr Mo Ni Elongation- 18% (min.)
0.150 1.50 1.00 0.04 0.025 11.5 0.5 1.0 Tensile strength- 620-795 Mpa.
max max. max. max. max – max max Hardness – 240 BHN max. (without
14.00 Heat Treatment.)
FOR CRUSHER PLATE
Advantage over the Disadvantage over the Mechanical Composition Area of Application
Martensitic steel Martensitic steel Elongation Tensile Hardness
Material (%) Strength (BHN)
(Mpa)
This composite has the NOT suitable for slag - - 627 used for recycling industries (primary), quarries
Metal Matrix effect of combining the very recycling (too abrasive) or (primary), concrete and asphalt.
Composites (MMC) – hard surface of ceramic limestone (risk of metal
Ceramics with the useful mechanical stress due to too long
(Martensitic Steel properties of steel. These lifetime).
with Ceramic (martensitic ceramic) can
abrasives over the have two to four times the
Wear surfaces) life of standard martensitic
steel.