CONCRETE, IT’S INGREDIENTS &

PROPERTIES
 Concrete- composite construction
material
Cement + Coarse Aggregate + Fine Aggregate + Water + Chemical
Admixtures
In its simplest form, concrete is a mixture of paste and aggregates.

The word concrete comes from the Latin word "concretus" (meaning
compact or condensed).

Concrete solidifies and hardens after mixing with water and

placement due to a chemical process known as hydration.

The water reacts with the cement, which bonds the other components
together, eventually creating a robust stone-like material.

Concrete is used more than any other man-made material in the world. As
of 2006, about 7.5 cubic kms of concrete are made each year—more than
one cubic meter for every person on Earth.
 Depending on the quality and proportions of the ingredients used
in the mix, the properties of concrete vary almost as widely as
different kinds of stones.
AGGREGATES
Aggregate is the general term applied to those inert or chemically
inactive materials which, when bonded together by cement, form
concrete.
Most of the aggregates used are naturally occurring aggregates
such as crushed rock, gravel and sand.
Artificial and processed aggregates may be broken brick or crushed
air-cooled blast furnace slag.
 AGGREGATES
Aggregates, which account for 60 to 75 percent of the total volume of concrete,
are divided into two distinct categories.

Coarse Aggregate
▪ Aggregate size more than 4.75mm
▪ Gravels constitute the majority of coarse aggregate used in concrete with
crushed stone making up most of the remainder
Fine Aggregate
▪ Aggregate size less than 4.75mm
▪ Fine aggregates generally consist of natural sand or crushed stone with most
particles passing through a sieve.

Aggregate processing consists of crushing, screening, and washing the aggregate to

obtain proper cleanliness and gradation.

Once processed, the aggregates are handled and stored in a way that minimizes
segregation and degradation and prevents contamination.

Aggregates strongly influence concrete's freshly mixed and hardened properties,

mixture proportions, and economy
 SUITABILITY REQUIREMENTS FOR
AGGREGATES
Aggregate used for concrete construction is required to comply with the norms laid down in
IS: 383-1970 ‘Specification for coarse and fine aggregates from natural sources for concrete’.

Some of the important characters of the aggregates are:

▪ Strength
▪ Size
▪ Particle shape
▪ Surface texture
▪ Grading
▪ Impermeability
▪ Cleanliness
▪ Chemical inertness
▪ Physical and Chemical Stability at high temperatures
▪ Co-efficient of thermal expansion
▪ Cost

To summarize, the aggregate should be composed of inert mineral matter, should have high
resistance to attrition, should be clean, free from any adhering coating, dense, durable and
sufficiently strong to enable the full strength of the cement matrix to be developed.
 COARSE AGGREGATES
• The material retained on 4.75mm sieve is termed as coarse aggregate.
Natural gravels can be quarried from pits where they have been deposited by
alluvial or glacial action and are normally composed of flint, quartz, schist and
igneous rocks.
• Coarse aggregates are obtained by crushing various types of granites, hard lime
stone and good quality sand stones.
• When very high strength concrete is required, a very fine-grained granite is
perhaps the best aggregate.
Coarse grained rocks make harsh concrete, and need high proportion of sand and
high water/cement ratio to get reasonable degree of workability.
• Hard and closed-grained crystalline lime stones are very suitable for aggregate, is
cheap, but should be used only in plain concrete.
• The bricks should be clean, hard, well-burnt and free from mortar and should not
contain more than half percent of soluble sulphates. It should not be used for
reinforced concrete work, since it is porous and may corrode the reinforcement.
• Blast furnace slag, coal ashes, coke-breeze etc. may also be used as aggregates to
obtain light weight and insulating concrete of low strength.
 FINE AGGREGATES
• The material smaller than 4.75mm size is called fine aggregate.
• Natural sands are generally used as fine aggregate.
• Sand may be obtained from pits, river, lake or sea-shore.
• When obtained from pits, it should be washed to free it from clean and silt.
• Sea shore sand may contain chlorides which may cause efflorescence, and may
cause corrosion of reinforcement. Hence it should be thoroughly washed before
use.
• Angular grained sand produces good and strong concrete, because it has good
interlocking property, while round grained particles of sand do not afford such
interlocking.
 GRADING OF AGGREGATES
• Grading refers to the determination of the particle-size distribution for aggregate.
• Grading limits and maximum aggregate size are specified because
grading and size affect the amount of aggregate used as well as
cement and water requirements, workability, pumpability, and
durability of concrete.
• In general, if the water-cement ratio is chosen correctly, a wide
range in grading can be used without a major effect on strength.
• When gap-graded aggregate are specified, certain particle sizes of aggregate are
omitted from the size continuum.
• Gap-graded aggregate are used to obtain uniform textures in exposed aggregate
concrete.
• Close control of mix proportions is necessary to avoid segregation.
• The grading of the aggregate has a marked effect on the workability, uniformity,
and finishing qualities of concrete.
 WATER
• Water acts as lubricant for the fine and coarse aggregates and acts chemically with
the cement to form the binding paste for the aggregate and reinforcement.
• Water is also used for curing the concrete after it has been cast into the forms.
• Water used for both mixing and curing should be free from injurious amount of
deleterious materials.
• Portable waters are generally considered satisfactory for mixing and curing of
concrete.
• Less water in the cement paste will yield a stronger, more durable concrete; more
water will give an freer-flowing concrete with a higher slump.
• Impure water used to make concrete can cause problems when setting or in causing
premature failure of the structure.
• Hydration involves many different reactions, often occurring at the same time.
• As the reactions proceed, the products of the cement hydration process gradually
bond together the individual sand and gravel particles and other components of the
concrete, to form a solid mass.
 WATER - CEMENT RATIO
• Water-Cement ratio is the ratio of volume of water mixed in concrete to volume of cement
used.
• The strength and workability of concrete depend to a great extent on the amount of water
used.
• For a given proportion of the materials, there is an amount of water which gives the greatest
strength.
• Amount of water less than this optimum water decreases the strength and about 10 percent
less may be insufficient to ensure complete setting of cement.
• More, than optimum water increases the workability but decrease the strength. An increase
in 10% above the optimum may decrease the strength approximately by 15% while an
increase in 50% may decrease the strength to one-half.
• The use of an excessive amount of water not only produces low strength but increases
shrinking, and decreases density and durability.
• According to Abram’s Water-Cement Ratio law, lesser the water-cement ratio in a workable
mix, greater will be its strength.
• According to Powers, cement does not combine chemically with more than half the quantity
of water in the mix.
• Water-cement ratio needs to be about 0.25 to complete the hydration reaction.
Typical values of w/c are between 0.35 and 0.40 because they give a good amount of
workability without sacrificing a lot of strength.
 ADMIXTURES
• Chemical admixtures are the ingredients in concrete other than portland cement,
water, and aggregate that are added to the mix immediately before or during
mixing.

Producers use admixtures primarily

▪ To reduce the cost of concrete construction;
▪ To modify the properties of hardened concrete;
▪ To ensure the quality of concrete during mixing, transporting, placing, and
curing; and
▪ To overcome certain emergencies during concrete operations.
• Most admixtures are supplied in ready-to-use liquid form and are added to the
concrete at the plant or at the jobsite.
• Certain admixtures, such as pigments, expansive agents, and pumping aids are
used only in extremely small amounts and are usually batched by hand from
premeasured containers.
• The effectiveness of an admixture depends on several factors including:
▪ Type and amount of cement,
▪ Water content,
▪ Mixing time,
▪ Slump, and
▪ Temperatures of the concrete and air.
• Sometimes, effects similar to those achieved through the addition of admixtures
can be achieved by altering the concrete mixture-reducing the water-cement ratio,
adding additional cement, using a different type of cement, or changing the
aggregate and aggregate gradation.
 ADMIXTURES
• Five Functions
Admixtures are classed according to function. There are five distinct classes of
chemical admixtures:
air-entraining, water-reducing, retarding, accelerating, and plasticizers (super
plasticizers).

• All other varieties of admixtures fall into the specialty category whose functions
include corrosion inhibition, shrinkage reduction, alkali-silica reactivity reduction,
workability enhancement, bonding, damp proofing, and coloring.

• Air-entraining admixtures, which are used to purposely place microscopic air

bubbles into the concrete, are discussed more fully in "Air-Entrained Concrete.“

• Water-reducing admixtures usually reduce the required water content for a

concrete mixture by about 5 to 10 percent.
• Consequently, concrete containing a water-reducing admixture needs less water to
reach a required slump than untreated concrete.

• The treated concrete can have a lower water-cement ratio. This usually indicates
that a higher strength concrete can be produced without increasing the amount of
cement.

• Recent advancements in admixture technology have led to the development of

mid-range water reducers.

• These admixtures reduce water content by at least 8 percent and tend to be more
stable over a wider range of temperatures. Mid-range water reducers provide
more consistent setting times than standard water reducers.
 ADMIXTURES
• Retarding admixtures, which slow the setting rate of concrete, are used to
counteract the accelerating effect of hot weather on concrete setting.
• High temperatures often cause an increased rate of hardening which makes placing
and finishing difficult.
• Retarders keep concrete workable during placement and delay the initial set of
concrete.
• Most retarders also function as water reducers and may entrain some air in
concrete.
• Accelerating admixtures increase the rate of early strength development, reduce
the time required for proper curing and protection, and speed up the start of
finishing operations.
• Accelerating admixtures are especially useful for modifying the properties of
concrete in cold weather.
• Superplasticizers, also known as plasticizers or high-range water reducers (HRWR),
reduce water content by 12 to 30 percent and can be added to concrete with a
low-to-normal slump and water-cement ratio to make high-slump flowing
concrete.
• Flowing concrete is a highly fluid but workable concrete that can be placed with
little or no vibration or compaction.
• The effect of super plasticizers lasts only 30 to 60 minutes, depending on the brand
and dosage rate, and is followed by a rapid loss in workability. As a result of the
slump loss, super plasticizers are usually added to concrete at the jobsite.
 ADMIXTURES
• Corrosion-inhibiting admixtures fall into the specialty admixture category and are
used to slow corrosion of reinforcing steel in concrete.
• Corrosion inhibitors can be used as a defensive strategy for concrete structures,
such as marine facilities, highway bridges, and parking garages, that will be
exposed to high concentrations of chloride.
• Other specialty admixtures include shrinkage-reducing admixtures and alkali-silica
reactivity inhibitors.
• The shrinkage reducers are used to control drying shrinkage and minimize cracking,
while ASR inhibitors control durability problems associated with alkali-silica
reactivity.
DISINTEGRATION AND DECAY OF CONCRETE

• Use of unsound cement, which due to some delayed chemical

reactions, undergo volume changes after the concrete has
hardened.
• Use of less durable aggregate, which may either react with
cement, or may be reacted upon by atmospheric gases.
• Entry of harmful gases and salts through excessive pores and voids
present in unsound concrete, causing its disintegration.
• Freezing and thawing of water sucked through the cracks or
crevices, by capillary action causing its disintegration.
Expansion and contraction resulting from temperature changes or
alternate wetting drying.
 DURABILITY
• The important properties of concrete, which govern the design of a concrete mix
are
▪ Strength
▪ Durability
▪ Workability
▪ Economy.
• Capable of resisting its disintegration and decay.
• The concrete should be durable with regard to the various weathering conditions
such as action of atmospheric gases, moisture changes, temperature variations.
• For durable concrete, water-cement ratio should be as small as possible to get a
workable mix.
• A well – compacted concrete has less voids and pores and has more durability.
• To entrap innumerable minute air bubble in concrete, Vinsol resin, is sometimes
mixed with concrete.
• To Prevent Vinsol resin reacting chemically with the cement, and to make it soluble
in water, it is first neutralised by the addition of sodium hydroxide.
 WORKABILITY
• It is difficult to properly define and measure the ‘workability’ of concrete, despite
its being the most important property.
• In its simplest form, the term ‘workability’ may be defined as the ease with which
concrete may be mixed, handled, transported, placed in position and compacted.
• According to Indian Standards, Workability of concrete is that property of concrete
which determines the amount of internal work necessary to produce full
compaction.
• The greatest single factor affecting the workability is the amount to water in the
mix.
• A workable concrete does not show any bleeding or segregation.
• Bleeding of concrete takes place when excess of water in the mix comes up at the
surface, causing small pores through the mass of the concrete.
• Segregation is caused when coarse aggregate separate out from the finer
materials, resulting in large voids, less durability and less strength.
• Concrete has relatively high compressive strength, but much lower
tensile strength.
For this reason is usually reinforced with materials that are strong
in tension (often steel).
The elasticity of concrete is relatively constant at low stress levels
but starts decreasing at higher stress levels as matrix cracking
develops.
Concrete has a very low coefficient of thermal expansion and
shrinks as it matures.
All concrete structures will crack to some extent, due to shrinkage
and tension.
Concrete that is subjected to long-duration forces is prone to
creep.
Tests can be made to ensure the properties of concrete
correspond to specifications for the application
 REINFORCEMENT
• Concrete is strong in compression, as the aggregate efficiently carries the
compression load.
• It is weak in tension as the cement holding the aggregate in place can crack,
allowing the structure to fail.
• Reinforced concrete solves these problems by adding either steel reinforcing bars,
steel fibers, glass fiber, or plastic fiber to carry tensile loads. Thereafter the
concrete is reinforced to withstand the tensile loads upon it.
• For a strong, ductile and durable construction the reinforcement
▪ shall have the following properties:
▪ High strength
▪ High tensile strain
▪ Good bond to the concrete
▪ Thermal compatibility
 REINFORCEMENT
• Steel reinforcement used in reinforced concrete may be of the following types:
(a) 1. Mild steel bars
2. Hot rolled Mild steel deformed bars
(b) 1. Medium tensile steel
2. Hot rolled medium tensile steel deformed bars
(C) 1. Hot rolled high yield strength deformed bars.
2. Cold-worked steel high strength deformed bars.
(d) 1. Hard drawn steel wire fabric
2. Rolled steel made from structural steel
 CONCRETING PROCESS
• Concreting Process involves the following
Process

Mixing of Transporting Placing Curing

Compactin
Concrete Concrete Concrete Concrete
g Concrete
 MIXING
The operation of manufacture of concrete is called ‘mixing’. The mixing can be
done by two methods:

HAND MIXING

• Mixing is done manually on a steel plate,, 2m x 2m in size or on a clean hard

surface.

• This method is resorted to when the quantity of concrete needed for the work is
small.

• Sand and cement in appropriate proportions are mixed first in a dry state.

• The coarse aggregate is then added and the whole mixture is mixed thoroughly
with the help of shovels.

• The predetermined amount of water is then sprinkled over the mix, till the colour
of concrete obtained is homogeneous and workable mix is obtained.
 MIXING
• MACHINE MIXING

Concrete should normally be mixed in a mechanical mixer. The main part

of the mixer is a drum in which the ingredients are mixed thoroughly by
mechanically rotating the drum.

The drum is made of steel plates, with a number of blades put in inclined
position in the drum.

As the drum rotates, the materials encounter resistance to rotation from the
blades and this disturbing effects helps in a good mixing of the ingredients.

The mixers are either operated electrically or else are driven by oil engines
attached to them.

Coarse aggregate should be fed first, then sand and lastly cement.
In the revolving state, when the three get thoroughly mixed, water should be
added either with the help of a can or automatically through the pipe attached to
the mixer.

Mixing should be continued until there is a uniform distribution of the materials

and the mass is uniform in colour and consistency, but in no case shall the mixing
be done for less than two minutes.

Concrete mixers may be of two types:

Batch Mixers
Continuous Mixers

Batch type mixers are employed for work of relatively small magnitude.

Batch type mixers can either be of tilting drum type or closed drum type. In the
tilting drum type, drum rotates about a trunnion axis and is so arranged that it is
quiet easy to rotate and tilt it when it is empty as well as when full.

In the close drum type, the drum remains rotating in one direction and is emptied
by means of the hopper which tilts to receive the discharge.

Continuous mixers are used in mass concreting work where a large and continuous
flow of concrete is required.
In these mixtures, processes of feeding, mixing and emptying go on continuously
without break.
 TRANSPORTING
• Concrete should be handled from the place of mixing to the place of final deposit
as rapidly as practical by methods which will prevent the segregation or loss of any
of the ingredients.
• If the segregation does occur during transport, the concrete should be remixed
before being placed.
• During hot or cold weather, concrete should be transported in deep containers, on
account of their lower ration of surface area to mass, reduce the rate of loss of
water by evaporating during hot weather and loss of heat during cold weather.
 PLACING
• The concrete should be placed and compacted before setting commences and
Should not subsequently be disturbed.

• Method of placing should be such as to preclude segregation.

• Before concrete is placed, it should be ensured that the forms are rigid, in their correct
position, well cleaned and oiled.

• Oiling of these forms will prevent the concrete from sticking to it, and it will then be
easier to remove the forms when they are no longer required.

• Concrete should not be poured into the forms only at one point, but should be
uniformly spread on all the sides for better compaction.

• When the work has to be resumed on a surface which has hardened, such surface
should be roughened.
• It should then be swept clean, thoroughly wetted and covered with a 13mm layer
of mortar composed of cement and sand in the same ratio as the cement and sand
in the concrete mix.

• This 13mm layer of mortar should be freshly mixed and placed immediately before
the placing of the concrete.

• Where the concrete has not fully hardened, all lattance should be removed by
scrubbing the wet surface with wire or bristle brushes, care being taken to avoid
dislodgement of particles of aggregate.
 PLACING
• The Surface should be thoroughly wetted and all free water removed.
• The surface should then be coated with neat cement grout.
• The first layer of concrete to be placed on this surface should not exceed 150mm in
thickness, and should be well –rammed against old work, particular attention being
paid to corners and close spots.
 COMPACTING
• The removal of entrapped air during production of concrete and the uniform,
dense arrangement of the constituents of concrete are effected during the
compacting of corners.
• The density and consequently, the strength and durability of concrete depend
upon this operation.
• Concrete should be thoroughly compacted during the operation of placing and
thoroughly worked around the reinforcement, around embedded fixtures and into
corners of the form work.
• Concrete is compacted by vibration, during which the vibrator communicates rapid
vibrations of low amplitude to the particles, as a result of which the concrete
becomes fluid, that is to say, its mobility is increased, and the particles, in
movement, under the force of gravity occupy a more stable position, which volume
of concrete is least.
• Vibrators are of three general types:
Internal Vibrators,
External Vibrators,
Surface Vibrators.
• Internal or immersion vibrators consists of a vibrating element enclosed in a casing
which is immersed in fresh concrete and transmit vibrations through the vibrator
body.
• External or form vibrators are fastened to the form work by a clamping device and
transmit vibrations to the concrete through the form.
• In precast members of concrete, the vibrating tables are very helpful. These tables
vibrate the entire mass of concrete uniformly.
 COMPACTING
• Surface vibrators, set up on the concrete surface after placing, transmit vibrations
to it through a working platform. They are generally employed in concrete road
construction.
• Mechanical method of compacting the concrete is used only when the mix is stiff.
• Over-vibration or vibration of very wet mixes is harmful and should be avoided.
Alternatively, concrete may be compacted manually by rodding, temping or
hammering.
• Rodding is generally done to compact thin vertical members while temping is done
for compacting concrete for slabs etc.,

CURING

• Curing is one of the most essential operation in which concrete is kept

continuously damp for some days to enable the concrete to gain more strength.
• Curing replenishes the loss of moisture from the concrete due to evaporation,
absorption and heat of reactions.
• The period of curing depends upon atmospheric conditions such as temperature,
humidity and wind velocity.
• The normal period is between 7 and 10 days.
 CURING
• There are several methods of curing the concrete, the more
common being the following:

Covering the exposed surface with a layer of sacking, canvas,

hessian or similar absorbant materials, and keeping them
continuously wet.

Thoroughly wetting the surface of concrete, and then keeping it

covered with a layer of suitable water proof material,

Impounding water in earthen or sandy bunds in squares over the

flooring,
Curing with the help of steam or hot water, resulting in rapid
development of strength.
 CONCRETE MIX DESIGN
• The process of selecting suitable ingredients of concrete and determining their
relative amounts with the objective of producing a concrete of the required,
strength, durability, and workability as economically as possible, is termed the
concrete mix design.
• The proportioning of ingredient of concrete is governed by the required
performance of concrete in 2 states, namely the plastic and the hardened states.
If the plastic concrete is not workable, it cannot be properly placed and
compacted. The property of workability, therefore, becomes of vital importance.
 PROPORTIONING
• The key to achieving a strong, durable concrete rests in the careful proportioning
and mixing of the ingredients.

• A concrete mixture that does not have enough paste to fill all the voids between
the aggregates will be difficult to place and will produce rough, honeycombed
surfaces and porous concrete.
• A mixture with an excess of cement paste will be easy to place and will produce a
smooth surface; however, the resulting concrete is likely to shrink more and be
uneconomical.
• A properly designed concrete mixture will possess the desired workability for the
fresh concrete and the required durability and strength for the hardened concrete.
• Typically, a mix is about 10 to 15 percent cement, 60 to 75 percent aggregate and
15 to 20 percent water.
Entrained air in many concrete mixes may also take up another 5 to 8 percent.
 MEASUREMENT OF MATERIALS
The compressive strength of hardened concrete which is generally considered to
be an index of its other properties, depends upon many factors, e.g. quality and
quantity of cement, water and aggregates; batching and mixing; placing,
compaction and curing.

CEMENT - Preferable to measure cement in terms of its weight, and not in terms of
volume.
FINE AGGREGATES - May be measured by weight for accurate works and by
volume for ordinary works. When dry sand absorbs water from atmosphere, or
when water is mixed to it artificially, its volume increases. This increases in volume
due to moisture in sand is known as bulking of sand. Hence, for accurate and large
scale works, sand is always measured by weight and necessary allowance is made
for the hygroscopic moisture in the sand.
COARSE AGGREGATE – No problem of bulking in coarse aggregate, and hence it
may be measured either by volume or by weight. But, for accurate and large scale
works, measurement should be done by weight.

WATER – Normally measured by volume, and specified as so many litres per bag of
cement.
For a given quantity of water to be mixed in concrete, adjustments should be made
for the amount of water present in sand and aggregate.
However, if the aggregate is dry and found to absorb water, extra water should be
added to account for this.
 METHODS OF CONCRETE MIX DESIGN

• The mix design methods being followed in different countries are mostly based on
empirical relationships, charts and graphs developed from extensive experimental
investigations.

• Following methods are in practice

1. ACI Mix design method

2. USBR Mix design method
3. British Mix design method
4. Mix design method according to Indian standard

Since ACI Mix design method is an originator for all other methods, including
Indian standard method, wherein every table and charts are fully borrowed from
ACI, so we follow the ACI Mix design method in practice
REQUIREMENTS OF CONCRETE MIX DESIGN

The requirements which form the basis of selection and proportioning of mix
ingredients are :
a ) The minimum compressive strength required from structural consideration
b) The adequate workability necessary for full compaction with the compacting
equipment available.
c) Maximum water-cement ratio and/or maximum cement content to give
adequate durability for the particular site conditions
d) Maximum cement content to avoid shrinkage cracking due to temperature cycle
in mass concrete.
 FACTORS IN CONCRETE MIX DESIGN

• The design of concrete mix will be based on the following factors.

(a) Grade of concrete:
This gives the characteristic strength requirements of concrete.
Depending upon the level of quality control available at the site, the
concrete mix has to be designed
for a target mean strength which is higher than the characteristic strength.
(b) Type of cement:
The type of cement is important mainly through its influence on the rate
of development of compressive strength of concrete as well as durability
under aggressive environments ordinary Portland cement(OPC) and
Portland Pozzolona cement (PPC) are permitted to use in reinforced
concrete construction.
(c) Maximum nominal size of aggregate:
It is found that larger the size of aggregate, smaller is the cement
requirement for a particular water cement ratio. Aggregates having a
maximum nominal size of 20mm or smaller are generally considered
satisfactory.
 FACTORS IN CONCRETE MIX DESIGN
• (d) Minimum water cement ratio:
The minimum w/c ratio for a specified strength depends on the type of cement.
(e) Workability:
The workability of concrete for satisfactory placing and compaction is related to
the size and shape of the section to be concreted.

TYPES OF MIXES

1. Nominal Mixes
In the past the specifications for concrete prescribed the proportions of cement,
fine and coarse aggregates. These mixes of fixed cement-aggregate ratio which
ensures adequate strength are termed nominal mixes.
These offer simplicity and under normal circumstances, have a margin of strength
above that specified.
However, due to the variability of mix ingredients the nominal concrete for a given
workability varies widely in strength.
 TYPES OF MIXES
2. Standard mixes
• The nominal mixes of fixed cement-aggregate ratio (by volume) vary widely in
strength and may result in under- or over-rich mixes.

• For this reason, the minimum compressive strength has been included in many
specifications. These mixes are termed standard mixes.

• IS 456-2000 has designated the concrete mixes into a number of grades as

M10, M15, M20, M25, M30, M35 and M40.

• In this designation the letter M refers to the mix and the number to the
specified 28 day cube strength of mix in N/mm2.

• The mixes of grades M10, M15, M20 and M25 correspond approximately to
the mix proportions (1:3:6), (1:2:4), (1:1.5:3) and (1:1:2) respectively.
3. Designed Mixes

• In these mixes the performance of the concrete is specified by the designer

but the mix proportions are determined by the producer of concrete, except
that the minimum cement content can be laid down.
• This is most rational approach to the selection of mix proportions with specific
materials in mind possessing more or less unique characteristics.
 PROPERTIES
1. Compressive strength:
It is one of the most important properties of concrete and influences many other
describable properties of the hardened concrete. The mean compressive
strength required at a specific age, usually 28 days, determines the nominal
water-cement ratio of the mix.
The other factor affecting the strength of concrete at a given age and cured at a
prescribed temperature is the degree of compaction.
According to Abraham’s law the strength of fully compacted concrete is inversely
proportional to the water-cement ratio.

2. Workability:
The degree of workability required depends on three factors.
These are the size of the section to be concreted, the amount of reinforcement,
and the method of compaction to be used.
For the narrow and complicated section with numerous corners or inaccessible
parts, the concrete must have a high workability so that full compaction can be
achieved with a reasonable amount of effort.
This also applies to the embedded steel sections. The desired workability
depends on the compacting equipment available at the site.
 PROPERTIES
3. Durability
The durability of concrete is its resistance to the aggressive environmental
conditions.
High strength concrete is generally more durable than low strength concrete.
In the situations when the high strength is not necessary but the conditions of
exposure are such that high durability is vital, the durability requirement will
determine the water-cement ratio to be used.

4. Maximum nominal size of aggregate

In general, larger the maximum size of aggregate, smaller is the cement requirement
for a particular water-cement ratio, because the workability of concrete increases
with increase in maximum size of the aggregate.
However, the compressive strength tends to increase with the decrease in size of
aggregate.
IS 456:2000 and IS 1343:1980 recommend that the nominal size of the aggregate
should be as large as possible.

5. Grading and type of aggregate

The grading of aggregate influences the mix proportions for a specified workability
and water-cement ratio.
 PROPERTIES
Coarser the grading leaner will be mix which can be used.
Very lean mix is not desirable since it does not contain enough finer material to
make the concrete cohesive.
The type of aggregate influences strongly the aggregate-cement ratio for the
desired workability and stipulated water cement ratio.
An important feature of a satisfactory aggregate is the uniformity of the grading
which can be achieved by mixing different size fractions.

6. Quality Control
The degree of control can be estimated statistically by the variations in test results.
The variation in strength results from the variations in the properties of the mix
ingredients and lack of control of accuracy in batching, mixing, placing, curing and
testing.
The lower the difference between the mean and minimum strengths of the mix
lower will be the cement-content required. The factor controlling this difference is
termed as quality control.

Mix Proportion designations

The common method of expressing the proportions of ingredients of a concrete
mix is in the terms of parts or ratios of cement, fine and coarse aggregates. For
e.g., a concrete mix of proportions 1:2:4 means that cement, fine and coarse
aggregate are in the ratio 1:2:4 or the mix contains one part of cement, two parts
of fine aggregate and four parts of coarse aggregate. The proportions are either by
volume or by mass. The water-cement ratio is usually expressed in mass
 Tests
The slump tests are conducted to determine the workability of fresh concrete.
The apparatus used for doing slump test are Slump cone and Tamping rod.
i) The internal surface of the mould is thoroughly cleaned and applied with a light
coat of oil.
ii) The mould is placed on a smooth, horizontal, rigid and nonabsorbent surface.
iii) The mould is then filled in four layers with freshly mixed concrete, each
approximately to one-fourth of the height of the mould.
iv) Each layer is tamped 25 times by the rounded end of the tamping rod (strokes are
distributed evenly over the cross section).
v) The strokes for the second and subsequent layers should be penetrate into the
underlying layer.
vi) Bottom layer should be tamped through out its depth
vii) After the top layer is rodded, the concrete is struck off the level with a trowel or
the tamping rod.
viii) The mould is removed from the concrete immediately by raising it slowly in the
vertical direction.
ix) This allows the concrete to subside and the slump is measured immediately by
determining the difference between the highest of the mould and that of the
highest point of the slumped specimen.
• Three forms of slumps may occur. The first is a true slump, the second is known as
a shear slump and the third a collapse slump which is obtained with lean harsh or
very wet mixes.
• Any slump specimen which collapses or shears off laterally gives incorrect results
and if this occurs the test should be repeated with another sample.
• If in the repeat test also, the specimen should shear, the slump shall be measured
and the fact that the specimen sheared, shall be recorded.
• Generally, if shear and collapse slumps are obtained the concrete will be
unsatisfactory for placing.
Concrete is used to make
• Pavements,
• Pipe,
• Architectural structures,
• Foundations,
• Motorways/Roads,
• Bridges/Overpasses,
• Parking structures,
• Brick/Block walls and
• Footings for gates, fences and poles.

Reinforced concrete,
prestressed concrete and
precast concrete are the most widely used types of concrete functional
extensions in modern days.
The formwork or shuttering is a temporary construction used as a mould for the
structure in which concrete is placed and in which it hardens and matures.

The cost of form work may be upto 20 to 25% of the cost of structure in building
work and even higher in bridges.

The operation of removing the formwork is commonly known as stripping.

The components of formwork are removed and then reused for the forms of
another part of the structure.

Such forms, whose components can be reused several times are known as panel
forms.

Forms are classified as wooden, plywood, steel, combined wood-steel, reinforced

concrete and plain concrete.
Timber is the most common material used for form work.
The disadvantages of the wooden form work is the possibility of
warping, swelling and shrinkage of the timber.

However those defects can be overcome by applying to the shuttering

water impermeable coatings.
This coating also prevents the shuttering from adhering to concrete
and hence makes the stripping easier.
• Steel shuttering is used for major work where every thing is mechanised. Steel
form work has many advantages, such as follows:
• It can be put to high number of uses
• It provides ease of stripping
• It ensures an even and smooth concrete surface
• It possesses greater rigidity
• It is not liable to shrinkage or distortion. However, steel form work is
comparatively more costly.

A good form work should satisfy the following requirements:

• The material of the form work should be cheap and it should be suitable for
re-use several times
• It should be practically water proof so that it does not absorb water from
concrete. Also, its shrinkage and swelling should be minimum
• It should be strong enough to withstand all loads coming on it, such as dead
load of concrete and live load during its pouring, compaction and curing
• It should be stiff enough so that deflection is minimum
• It should be as light as possible
• The surface of the form work should be smooth, and it should afford easy
stripping
• All joints of the form works should be stiff so that lateral deformation under
loads is min.
• The form work should rest on non-yielding supports.
 Concrete expands and shrinks with changes in moisture and temperature.
The over all tendency is to shrink and this can cause cracking at an early stage.
Irregular cracks are unsightly and difficult to maintain but generally do not affect
the integrity of the concrete.
Joints are simply pre planned cracks.
Joints can be created by forming, tooling, sawing and placement of joint formers.

There are 3 common types of Concrete Joints:

CONTRACTION JOINTS

Contraction joints are purposely installed joints designed to regulate cracking that
might otherwise occur due to the unavoidable, often unpredictable contraction of
concrete.
These joints are often called control joints because they are intended to control
crack locations.
The necessary plane of weakness may be formed by reducing the concrete
cross-section by tooling or saw cutting a joint within 24 hours of placing.
Contraction joint movement is supposed to be small.
CONSTRUCTION JOINTS
• Construction joints are made before and after interruptions in the placement of
concrete or through the positioning of precast units.
• Locations are usually predetermined so as to limit the work that can be done at
one time to a convenient size, with least impairment of the finished structure,
though they may also be necessitated by unforeseen interruptions in concreting
operations.
• Depending on the structural design, they may be required to function later as
expansion or contraction joints or they may be required to be soundly bonded to
the first so as to maintain complete structural integrity.
• Construction joints may run horizontally or vertically depending on the placing
sequence prescribed by the design of the structure.
EXPANSION JOINTS
• Expansion joints are designed to prevent the crushing and distortion of the
absorbing concrete structural units that might otherwise occur due to the
transmission of compressive forces that may be developed by expansion,
applied loads, or differential movements arising from the configuration of the
structure or its settlement.
• Expansion joints are made by providing a space over the entire cross section
between abutting structural units.
Thank you!!!!!